Research of Gradient Wear-resisting Coating Produced by Laser Additive Manufacturing on High-pressure Pump Camshaft

  • SHI Yan ,
  • LI Yunfeng ,
  • LIU Jia ,
  • YUAN Zhenyu
Expand
  • School of Electromechanical Engineering，Changchun University of Science and Technology， Changchun 130022)

Online published: 2017-03-20

Fold

Abstract

To improve the wear resistance and operational reliability of high-pressure pump camshaft. The research of gradient wear-resisting coating produced by laser additive manufacturing on complex morphology high-pressure pump camshaft using the 5 kW CO2 laser,four-axis CNC machines and the co-axial powder feeding system. Based on the research of the gradient coating,the edge anti-collapse fixture and the movement control of cam,and realized the preparation of uniform high-hardness gradient coating without defects and the good protection of cam’s edges. The macromorphology and microstructures are characterized by using laser microscope,SEM,XRD and microhardness tester. Comparison tests of service lives of the additive manufacturing camshafts and the cemented quenching camshafts are carried out on the high pressure pump test-bed. The results show that the primary phases of gradient coating are γ-Co solid solution,Co3B,M23C6 and etc. The reinforcing phases are WC and W2C in transition layers and wear-resisting layer. The microstructures of gradient coating contains primary dendrites and interdendritic eutectics. The metallurgical bonding forms well between the gradient coating and the cam. Compared with the cemented quenching camshafts,the useful life of the additive manufacturing camshafts is increased by 65%.

Key words： laser additive manufacturing; camshaft; gradient coating; microstructure; wear resistance

Cite this article

SHI Yan , LI Yunfeng , LIU Jia , YUAN Zhenyu . Research of Gradient Wear-resisting Coating Produced by Laser Additive Manufacturing on High-pressure Pump Camshaft[J]. Journal of Mechanical Engineering, 2017 , 53(6) : 80 -87 . DOI: 10.3901/JME.2017.06.080

References

 [1] 王大承. HT300摩托车凸轮轴激光表面强化处理研究[J]. 激光技术，2002，26(6)：474-477.
 WANG Dacheng. Research of laser surface strengthening technique for HT300 camshaft of motorcycle[J]. Laser Technology，2002，26(6)：474-477.
 [2] 李双寿，陆劲昆，边庆月，等. 球墨铸铁凸轮轴的激光表面熔凝处理[J]. 金属热处理，2005，30(2)：4-8.
 LI Shuangshou，LU Jinkun，BIAN Qingyue，et al. Laser surface melting process for camshaft made of ductile iron[J]. Heat Treatment of Metals，2005，30(2)：4-8.
 [3] 卢求元，赵俊平. 发动机凸轮表面耐磨减摩薄膜的制备与表征[J]. 金属热处理，2015，40(6)：171-174.
 LU Qiuyuan，ZHAO Junping. Preparation and characterization of films with high wear resistance and low friction coefficient on engine cam surface[J]. Heat Treatment of Metals，2015，40(6)：171-174.
 [4] RICCIARDI G，CANTELLO M. Surface treatment of automobile parts by rtm[J]. SPIE Vol.957，Laser Beam Surface Treating and Coating，1988：66-74.
 [5] 石岩，张宏，刘双宇，等. 高硬度多微孔小型零件激光表面精密熔覆钴基合金涂层提高耐冲蚀性能研究[J]. 机械工程学报，2011，47(2)：95-101.
 SHI Yan，ZHANG Hong，LIU Shuangyu，et al. Improving resistance of cobalt-based alloy coating formed laser fine cladding on high-hardness and microporous small parts[J]. Journal of Mechanical Engineering，2011，47(2)：95-101.
 [6] RIABKINA-FISHMAN M，RABKIN E，LEVIN P，et al. Laser produced functionally graded tungsten carbide coatings on M2 high-speed tool steel[J]. Materials Science and Engineering，2001，302(1)：106-114.
 [7] 张国栋，杨辉，王麒瑜，等. 铁素体不锈钢激光熔覆层组织和性能研究[J]. 机械工程学报，2016，52(12)：37-45.
 ZHANG Guodong，YANG Hui，WANG Qiyu，et al. Microstructure and properties of laser cladding layer on ferritic stainless steel[J]. Journal of Mechanical Engineering，2016，52(12)：37-45.
 [8] 赵彦华，孙杰，李剑峰，等. KMN钢激光熔覆FeCr合金修复层组织性能及耐磨、耐蚀性研究[J]. 机械工程学报，2015，51(8)：37-43.
 ZHAO Yanhua，SUN Jie，LI Jianfeng，et al. Research on microstructure properties and wear and corrosion resistance of FeCr repaired coating on kmn steel by laser cladding[J]. Journal of Mechanical Engineering，2015，51(8)：37-43.
 [9] 王新洪，张敏，邹增大，等. 激光熔覆TiCp Ni基合金复合涂层的显微组织与性能[J]. 机械工程学报，2003，39(2)：37-41.
 WANG Xinhong，ZHANG Min，ZOU Zengda，et al. Microstructure and properties of laser clad TiCp/Ni-based alloys composite coating[J]. Chinese Journal of Mechanical Engineering，2003，39(2)：37-41.
[10] MAJUMDAR D J，CHANDRA R B，NATHB K A，et al. Studies on compositionally graded silicon carbide dispersedcomposite surface on mild steel developed by laser surface cladding[J]. Journal of Materials Processing Technology，2008，1：505-512.
[11] 沈斌，闫广超，吴钢. 复杂盘形凸轮表面激光熔覆工艺[J]. 中国激光，2009，36(1)：244-248.
 SHEN Bin，YAN Guangchao，WU Gang. Laser cladding on complex disc cam[J]. Chinese Journal of Laser，2009，36(1)：244-248.
[12] 董世运，张晓东，徐滨士，等. 45钢凸轮轴磨损凸轮的激光熔覆再制造[J]. 装甲兵工程学院学报，2011，25(2)：85-87.
 DONG Shiyun，ZHANG Xiaodong，XU Binshi，et al. Laser cladding remanufacturing of 45 steel camshaft worn cam[J]. Journal of Academy of Armored Force Engineering，2011，25(2)：85-87.
[13] 宋建丽，邓琦林，陈畅源，等. 宽带激光熔覆高硬度火焰喷涂层组织和裂纹行为[J]. 机械工程学报，2006，42(12)：169-174.
 SONG Jianli，DENG Qilin，CHEN Changyuan，et al. Microstructure and cracking behavior of wide-band laser cladding flame sprayed high hardness coatings[J]. Chinese Journal of Mechanical Engineering，2006，42(12)：169-174.
[14] 余廷，邓琦林，董刚，等. 钽对激光熔覆镍基涂层的裂纹敏感性及力学性能的影响[J]. 机械工程学报，2011，47 (22)：25-30.
 YU Ting，DENG Qilin，DONG Gang，et al. Influence of Ta on crack susceptibility and mechanical properties of laser clad ni-based coating[J]. Journal of Mechanical Engineering，2011，47 (22)：25-30.
[15] 陈列，陶然，刘顿，等. 斜齿面激光熔覆的开裂倾向分析及控制研究[J]. 中国激光，2014，41(11)：1-7.
 CHEN Lie，TAO Ran，LIU Dun，et al. Analysis and control the cracking tendency on helical tooth surface during laser cladding[J]. Chinese Journal of Laser，2014，41(11)：1-7.
[16] WANG Dengzhi，HU Qianwu，ZENG Xiaoyan. Residual stress and cracking behaviors of Cr13Ni5Si2 based composite coatings prepared by laser-induction hybrid cladding[J]. Surface and Coatings Technology，2015，274(6)：51-59.
[17] 张栋栋. 高硬度激光熔覆层裂纹的产生机理及控制方法研究[D]. 长春：长春理工大学，2013.
 ZHANG Dongdong. Study on the generating mechanism and control methods of high hardness laser cladding
 
 coating cracks[D]. Changchun：Changchun University of Science and Technology，2013.
[18] 陈列，谢沛霖. 齿面激光熔覆中的防边缘塌陷工艺研究[J]. 激光技术，2007，31(5)：518-521.
 CHEN Lie，XIE Peilin. Research of preventing the edges of tooth surface from collapsing in laser-cladding process[J]. Laser Technology，2007，31(5)：518-521.
[19] 袁庆龙，冯旭东，曹晶晶，等. 激光熔覆镍基合金涂层微观组织研究[J]. 中国激光，2010，37(8)：2116-2120.
 YUAN Qinglong，FENG Xudong，CAO Jingjing，et al Research on microstructure of Ni-Based alloy coating by laser cladding[J]. Chinese Journal of Laser，2010，37(8)：2116-2120.
Options
Outlines

/

〈 〉

　 Copyright © Journal of Mechanical Engineering, All Rights Reserved.
Powered by Beijing Magtech Co. Ltd,.