Microstructure and Mechanical Properties of Al-Cu Joints by Cold Spray Bonding

FU Silin; LI Chengxin; WEI Yingkang; LUO Xiaotao; YANG Guanjun; LI Jinglong; LI Changjiu

doi:10.3901/JME.2018.10.093

Journal of Mechanical Engineering >

2018 , Vol. 54 >Issue 10: 93 - 102

DOI: https://doi.org/10.3901/JME.2018.10.093

Microstructure and Mechanical Properties of Al-Cu Joints by Cold Spray Bonding

FU Silin ,
LI Chengxin ,
WEI Yingkang ,
LUO Xiaotao ,
YANG Guanjun ,
LI Jinglong ,
LI Changjiu

Expand

1. State Key Laboratory for Mechanical Behavior of Materials, Xi'an Jiao Tong University, Xi'an 710049;
2. Shaanxi Key Laboratory of Friction Welding Technologies, Northwestern Polytechnical University, Xi'an 710072

Received date: 2017-06-19

Revised date: 2017-12-14

Online published: 2018-05-20

Fold

Abstract

The cold spray bonding method had been applied to connect the pure aluminum and copper in ambient environment under nitrogen gas at 2.4 MPa and 270℃, which can eliminate the brittle intermetallic compounds of welded joints under fusion welding process due to the physical mismatches in densities, melting points and elasticity modules. In this method, solid-state pure aluminum particles with high-speed impacted on the substrate. The stainless steel particles is added in the feedstocks that assisted to improve the mechanical properties of joints. The results of mechanical properties at the bonding joints show that the average tensile strength of bonded joints is about 63 MPa; the average shear strength of Cu-Al and Al-Al bonding interface is 38 MPa and 42 MPa, respectively. The joint is mainly connected to the base metals by mechanical interlocking; the plastic deformation of pure aluminum particles, the strength and density of bonded joints are significantly enhanced with the in-situ tamping effect from the stainless steel particles. The interlocking effect from the stainless steel particles embedded in the base materials can effectively improve the shear strength of the bonding joints.

Key words： cold spray bonding; cold spray; dissimilar metal joint; cold welding

Cite this article

FU Silin , LI Chengxin , WEI Yingkang , LUO Xiaotao , YANG Guanjun , LI Jinglong , LI Changjiu . Microstructure and Mechanical Properties of Al-Cu Joints by Cold Spray Bonding[J]. Journal of Mechanical Engineering, 2018 , 54(10) : 93 -102 . DOI: 10.3901/JME.2018.10.093

References

[1] 黄伯云. 我国有色金属材料现状及发展战略[J]. 中国有色金属学报,2004,14(5):122-127. HUANG Boyun. Status and developing strategy for China's nonferrous metal materials industry[J]. Transactions of Nonferrous Metals Society of China,2004,14(5):122-127.
[2] 韩培培,杨超,王继杰,等. 固溶处理对7B04-O铝合金搅拌摩擦焊接接头微观组织与力学性能的影响[J]. 机械工程学报,2015,51(22):35-41. HAN Peipei,YANG Chao,WANG Jijie,et al. Effects of solution heat treatment on friction stir welding joints of 7B04-O aluminum alloy[J]. Journal of Mechanical Engineering,2015,51(22):35-41.
[3] 马铁军,刘亚森,李文亚,等. 线性摩擦焊AA5083铝合金/T2纯铜异质接头特征研究[J]. 机械工程学报,2017,53(4):11-17. MA Tiejun,LIU Yasen,LI Wenya,et al. Characteristics of linear friction welded AA5083 aluminium alloy-T2 pure copper dissimilar joint[J]. Journal of Mechanical Engineering,2017,53(4):11-17.
[4] XIA C Z,LI Y J,PUCHKOV U A,et al. Microstructure and phase constitution near the interface of Cu/Al vacuum brazing using Al-Si filler metal[J]. Journal of Materials Science and Technology,2008,82(4):799-804.
[5] 刘正林,杨凯珍,尹登峰. 铝铜钎焊用Zn-Al钎料的研究[J]. 热加工工艺,2009,38(11):543-546. LIU Zhenglin,YANG Kaizhen,YIN Dengfeng. Study on Zn-Al solder used for Al/Cu brazing[J]. Hot Working Technology,2009,38(11):543-546.
[6] 何鹏,周世明,冯吉才. 铜-铝合金CPU散热器钎焊技术研究[J]. 材料科学与工艺,2006,14(5):123-128. HE Peng,ZHOU Shiming,FENG Jicai. A new technology for brazing of aluminum alloy to copper of CPU radiator[J]. Materials Science and Technology, 2006,14(5):123-128.
[7] NAKA M,HAFEZ K M. Applying of ultrasonic waves on brazing of alumina to copper using Zn-Al filler alloy[J]. Journal of Materials Science,2003,28(16):3491-3494.
[8] SCHBERT E,KLASSEN M,ZERNER I,et al. Light-weight structures produced by laser beam joining for future applications in automobile and aerospacee industry[J]. Journal of Materials Processing Technology,2001,115(1):2-8.
[9] SUN Z,ION J C. Laser-welding of dissimilar metal combinations[J]. Journal of Materials Science,1995,30(17):4205-4214.
[10] LI Yong,CHEN Shengle,HUANG Jinlong,et al. Experimental and simulation studies on cold welding sealing process of heat pipes[J]. Chinese Journal of Mechanical Engineering,2017,30(2):332-343.
[11] SUN Z. Joining dissimilar material combinations:materials and processes[J]. International Journal of Materials and Product Technology,1995,10(1-2):16-27.
[12] MAI T A,SPOWAGE A C. Characterisation of dissimilar joints in laser welding of steel-kovar, copper-steel and copper-aluminum[J]. Materials Science and Engineering:A,2004,374(1-2):224-233.
[13] 张洪涛,刘多,冯吉才,等. 铝/铜高频感应接触反应钎焊[J]. 焊接学报,2012,33(3):89-92. ZHANG Hongtao,LIU Duo,FENG Jicai,et al. Reactive contact brazing between aluminum alloy and copper by high frequency induction method[J]. Transactions of the China Welding Institution,2012,33(3):89-92.
[14] 吴铭方,司乃潮,蒲娟. 铝合金/铜/不锈钢接触反应钎焊[J]. 焊接学报,2009,30(11):85-88. WU Mingfang,SI Naichao,PU Juan. Contact reactive brazing between Al alloy/Cu/stainless steel and analysis on grain boundary penetration behaviors[J]. Transactions of the China Welding Institution,2009,30(11):85-88.
[15] 崔占全,李达,孔明辉,等. 7075铝合金与H68黄铜的搅拌摩擦焊组织分析[J]. 焊接学报,2011,32(7):91-94. CUI Zhangquan,LI Da,KONG Minghui,et al. Microstructure of friction stir welding joint of 7075Al and H68 brass[J]. Transactions of the China Welding Institution,2011,32(7):91-94.
[16] ABBASI M,KARIMI T A,SALEHI M T. Growth rate of intermetallic compounds in Al/Cu bimetal produced by cold roll welding process[J]. Journal of Alloys and Compounds,2001,319(1-2):233-241.
[17] HEIDEMAN R,JOHNSON C,KOU S. Metallurgical analysis of Al/Cu friction stir spot welding[J]. Science and Technology of Welding and Joining,2010,15(7):597-604.
[18] 刘会杰,刘向前,胡琰莹. 搅拌摩擦焊缝类型对接头拉伸性能及断裂特征的影响[J]. 机械工程学报,2015,51(22):29-34. LIU Huijie,LIU Xiangqian,HU Yanying. Effects of weld characteristics on tensile properties and fracture morphologies of friction stir welded joints[J]. Journal of Mechanical Engineering,2015,51(22):29-34.
[19] HUANG Renzhong,FUKANUMA H. Study of the influence of particle velocity on adhesive strength of cold spray deposits[J]. Journal of Thermal Science and Technology,2011,21:541-549.
[20] HUANG Renzhong,MICHIYOSHI S. The effects of heat treatment on the mechanical properties of cold-sprayed coating[J]. Surface and Coating Technology,2015,261:278-288.
[21] 李文亚,李长久. 冷喷涂特性[J]. 中国表面工程,2002,15(1):12-16. LI Wenya,LI Changjiu. Characteristics of cold spray process[J]. China Surface Engineering,2002,15(1):12-16.
[22] KARTHIKEYAN J,KAY C M,LINDEMAN J,et al. Cold spray processing of titanium powder[C]//Proc. of 1st ITSC'2000:255-262.
[23] 张志函,蒋若蓉,李文亚. 冷喷铝涂层对2024铝合金搅拌摩擦焊接头力学性能的影响[J]. 机械工程学报,2015,51(22):42-46. ZHANG Zhihan,JIANG Ruorong,LI Wenya. Influence of cold sprayed aluminum coating on the mechanical properties of friction stir welded 2024 aluminum alloy joints[J]. Journal of Mechanical Engineering,2015,51(22):42-46.
[24] ASSADI H,GARTENR F,STOLTENHOFF T,et al. Bonding mechanism in cold gas spraying[J]. Acta Materialia,2003,51(15):4379-4394.
[25] GRUJICIC M,ZHAO C L,DEROSSET W S,et al. Adiabatic shear instability based mechanism for particles/substrste bonding in the cold-gas dynamic spray process[J]. Materials and Design,2004,25(8):681-688.
[26] LI C J,LI W Y,WANG Y Y. Formation of metastable phases in cold-sprayed soft metallic deposit[J]. Surface and Coating Technology,2005,198(1-3):469-473.
[27] LUO X T,WEI Y K,WANG Y. Microstructure and mechanical property of Ti and Ti6Al4V prepared by an in-situ shot peening assisted cold spraying[J]. Materials and Design,2015,85:527-533.
[28] MURR L E,QUINONES S A,FERREYRA E T,et al. The low-velocity-to-hypervelocity penetration transition for impact craters in metal targets[J]. Materials Science and Engineering,1998,256:166-182.

Options

Outlines

模态框（Modal）标题

Abstract

Cite this article

References