为了研究微型面接触摩擦副在海水环境中的动力学和摩擦学性能，根据柱塞运动过程无刚性冲击和柔性冲击的准则，选取了B样条曲线、五次多项式曲线和正弦曲线作为研究对象，计算了微型面接触摩擦副接触应力以及摩擦应力；以动力学计算的结果对摩擦试验进行加载，筛选摩擦副材料。结果表明三种曲线组成的摩擦副接触应力最大值约为160 MPa，摩擦应力最大值均约为16 MPa，B样条曲线和正弦曲线综合力学性能优于五次多项式曲线。通过销盘摩擦试验考察了在初始接触应力约为160 MPa，滑动速度为0.5 m/s的工况下，纯PEEK、含有30%玻璃纤维的PEEK和分别含有10%石墨/碳纤维/PTFE的PEEK与17-4PH组成摩擦副的摩擦学性能。试验结果表明分别含有10%石墨/碳纤维/PTFE的PEEK与17-4PH摩擦副的摩擦因数和磨损量均最小，磨损机理为轻微的粘着磨损，可作为微型面接触摩擦副滚动体材料。
周杰
,
吴进军
,
于革刚
,
杨友胜
,
段海涛
,
易蒙
. 基于海水介质的微型面接触摩擦副应力及摩擦学研究[J]. 机械工程学报, 2018
, 54(3)
: 88
-94
.
DOI: 10.3901/JME.2018.03.088
In order to study the dynamic and tribological performance of micro contact surface in seawater, by the goals of no stiff impact and flexible impact, study focus on the contact pressure and tribological stress of B-spline curve, quantic polynomial curve and sine curve, and the friction experiments were carried out, with the results to select the material of friction pair. The results shows that the maximum contact stress is about 160 MPa, the maximum tribological stress is about 16 MPa. Moreover, the mechanical performance of B-spline curve and sine curve is better than quantic polynomial curve. The tribological behavior, of three kinds PEEK composites (pure PEEK, 30% glass fiber PEEK and 10% graphite/10% carbon fiber/10%PTFE PEEK) coupled with 17-4PH, were compared under seawater by pin-on-disc friction test, the operating condition is about 160 MPa and 0.5 m/s, results indicates that the wear and friction coefficient of 10% graphite/10% carbon fiber/10%PTFE PEEK and 17-4PH friction pair is minimum, the main mechanism is light abrasive wear, so 10% graphite/10% carbon fiber/10%PTFE PEEK composite is suitable for micro contact surface.
[1] 王树杰. 柔性叶片潮流能水轮机水动力学性能研究[D].青岛:中国海洋大学,2009. WANG Shujie. Study on hydrodynamic performances of a tidal current energy conversion device with flexible blade turbine[D]. Qingdao:Ocean University of China,2009.
[2] 高殿荣,王志强,温茂森,等. 径向低速大扭矩水液压马达定子曲线分析[J]. 燕山大学学报,2011,35(6):493-500. GAO Dianrong,WANG Zhiqiang,WEN Maosen,et al. Analysis of stator curve of low speed high torque water hydraulic motor with radial piston[J]. Journal of Yanshan University,2011,35(6):493-500.
[3] 黄瑶. 低速大扭矩水压马达受力分析与流场的数值模拟[D]. 秦皇岛:燕山大学,2013. HUANG Yao. Force analysis and numerical simulation of flow field of low-speed high torque water hydraulic motor[D]. Qinhuangdao:Yanshan University,2013.
[4] 胡波. 海水径向柱塞泵的研究[D]. 青岛:中国海洋大学,2014. HU Bo. The reasarch of water hydraulic radial piston pump[D]. Qingdao:Ocean University of China,2014.
[5] 翟江. 海水淡化高压轴向柱塞泵的关键技术研究[D]. 杭州:浙江大学,2012. ZHAI Jiang. Investigation into the key problems of axial piston pump for seawater desalination[D]. Hangzhou:Zhejiang University,2012.
[6] 杨曙东. 基于海水润滑的中高压海水液压泵研究[D]. 武汉:华中科技大学,2005. YANG Shudong. A dissertation submitted in partial fulfillment of the requirements for the degree of doctor of philosophy in engineering[D]. Wuhan:Huazhong University of Science and Technology,2005.
[7] YIN F L,NIE S L,ZHANG Z H,et al. Research on the sliding bearing pair of water hydraulic axial piston pump[J]. Journal of Mechanical Engineering Science,2013,227(9):2049-2063.
[8] ZHANG Z H,NIE S L,YUAN S H,et al. Comparative evaluation of tribological characteristics of CF/PEEK and CF/PTFE/Graphite filled PEEK sliding against AISI630 steel for seawater hydraulic piston pumps/motors[J]. Tribology Transactions,2015,58:1096-1104.
[9] 刘恒龙,柯坚,王志国,等. 水压滑靴副的润滑特性[J]. 机械工程学报,2006,42(3):36-39. LIU Huanlong,KE Jian,WANG Guozhi,et al. Lubrication characteristics of the water hydraulic sliding shoe pairs[J]. Chinese Journal of Mechanical Engineering,2006,42(3):36-39.
[10] MA L R,LUO J B,ZHANG C H. Effect of solid surface on the formation of thin confined lubricating film of water with micro-content of oil[J]. Applied Surface Science,2010,256(22):6574-6579.
[11] MA L R,LUO J B,ZHANG C H. Film forming characteristics of oil-in-water emulsion with super-low oil concentration[J]. Colloids & Surfaces A Physicochemical & Engineering Aspects,2009,340(1–3):70-76.
[12] SUMER M,UNAL H,MIMAROGLU A. Evaluation of tribological behavior of PEEK and glass fiber reinforced PEEK composite under dry sliding and water lubricated conditions[J]. Wear,2008,265(7):1061-1065.
[13] JIA J,CHEN J,ZHOU H,HU L. Comparative study on tribological behaviors of polyetheretherketone composite reinforced with carbon fiber and polytetrafluoroethylene under water-lubricated and dry-sliding against stainless steel[J]. Tribology letters,2004,17(2):231-238.
[14] CHEN B B,WANG J Z,YAN F Y. Comparative investigation on the tribological behaviors of CF/PEEK composites under sea water lubrication[J]. Tribology International,2012,52(3):170-177.
[15] UNAL H,MIMAROGL U. Friction and wear characteristics of peek and its composite under water lubrication[J]. Journal of Reinforced Plastics & Composites,2006,25(25):1659-1667.
[16] CHAIRMAN C,BABU S. Mechanical and abrasive wear behavior of glass and basalt fabric-reinforced epoxy composites[J]. Journal of Applied Polymer Science,2013,130(1):120-130.
[17] PEI X Q,BENNEWITZ R,SCHLARB A. Mechanisms of friction and wear reduction by carbon fiber reinforcement of PEEK[J]. Tribology Letters,2016,58(3):1-10.
[18] RODRIGUEZ V,SUKUMARAN J,ALOIS K S,et al. Influence of solid lubricants on tribological properties of polyetheretherketone(PEEK)[J]. Wear,2016,103:45-57.
[19] WANG J Z,YAN F Y,XUE Q J. Tribological behavior of PTFE sliding against steel in sea water[J]. Wear,2009,267(9-10):1634-1641.
[20] REFAIT P,ABDELMOULA M,GENIN J M R,et al. Green rusts in electrochemical and microbially influenced corrosion of steel[J]. Comptes Rendus Geoscience,2006,338 (6):476-487.