激光选区熔化（Selective laser melting，SLM）增材制造技术具备极端复杂构件制造能力，为高性能构件的材料结构一体化制造提供了技术支撑。然而，在激光与材料交互作用过程中，熔池稳定性，熔池间界面结合性，熔体与基体的润湿性等因素直接影响构件微观组织、表面精度与粗糙度。其中，SLM成形的金属表面粗糙度较高是制约其发展的重要因素，SLM技术与机加工复合是发展趋势之一。因此，采用机加工的方法对SLM样品进行表面处理，分别研究了机加工对不同致密度金属，不同铣削深度及不同铣削面对金属试样粗糙度及残余应力的影响规律。其中，试样粗糙度经过铣削后从约10 μm降低到1 μm以下，极大改善了制件的表面质量。同时，通过铣削使试样水平方向的残余应力由压应力变为拉应力并大幅降低。
章媛洁
,
宋波
,
赵晓
,
张李超
,
魏青松
,
史玉升
. 激光选区熔化增材与机加工复合制造AISI 420不锈钢:表面粗糙度与残余应力演变规律研究[J]. 机械工程学报, 2018
, 54(13)
: 170
-178
.
DOI: 10.3901/JME.2018.13.170
Selective laser melting has the ability to produce extremely complex components, providing technical support for materials and structures integrated manufacturing of high performance components. Stability of molten pool, interfacial bonding property of molten pool and wettability of melt and substrate have an influence on microstructure, surface precision and roughness of components during the interaction of laser and material. Thus, high surface roughness of SLMed parts limits its development. Selective laser melting and subtractive hybrid manufacture is one of the development trends. Therefore, the milling method is taken to improvement surface quality of SLM-processed samples. Influence of surface roughness and residual stress by different porosity, different milling depth and different milling surface is studied. Surface roughness has been greatly improved and decreased from 10 μm to 1 μm after milling. The horizontal direction residual stress of the sample has changed from compressive stress to tensile stress and reduced a lot by milling.
[1] 李瑞迪,史玉升,刘锦辉,等. 304L不锈钢粉末选择性激光熔化成形的致密化与组织[J]. 应用激光, 2009(5):369-373. LI Ruidi, SHI Yusheng, LIU Jinhui, et al. Densification and microstructure of 304L stainless steel fabricated via selective laser melting[J]. Applied Laser, 2009(5):369-373.
[2] 陈静,林鑫,王涛,等. 316L不锈钢激光快速成形过程中熔覆层的热裂机理[J]. 稀有金属材料与工程, 2003, 32(3):183-186. CHEN Jing, LIN Xin, WANG Tao, et al. The hot cracking mechanism of 316L stainless steel cladding in rapid laser forming process[J]. Rare Metal Materials and Engineering, 2003, 32(3):183-186.
[3] SIMCHI A. Direct laser sintering of metal powders:Mechanism, kinetics and microstructural features[J]. Materials Science and Engineering:A, 2006, 428(1):148-158.
[4] SONG B, ZHAO X, LI S, et al. Differences in microstructure and properties between selective laser melting and traditional manufacturing for fabrication of metal parts:A review[J]. Frontiers of Mechanical Engineering, 2015, 10(2):111-125.
[5] ABE F, OSAKADA K, SHIOMI M, et al. The manufacturing of hard tools from metallic powders by selective laser melting[J]. Journal of materials processing technology, 2001, 111(1):210-213.
[6] 刘睿诚,杨永强,王迪. 选区激光熔化成型金属零件上表面粗糙度的研究[J]. 激光技术, 2013, 37(4):425-430. LIU Ruicheng, YANG Yongqiang, WANG Di. Research of upper surface roughness of metal parts fabricated by selective laser melting[J]. Laser Technology, 2013, 37(4):425-430.
[7] GEBHARDT A, SCHMIDT F M, HÖTTER J S, et al. Additive manufacturing by selective laser melting the realizer desktop machine and its application for the dental industry[J]. Physics Procedia, 2010, 5:543-549.
[8] ATZENI E, IULIANO L, MINETOLA P, et al. Proposal of an innovative benchmark for accuracy evaluation of dental crown manufacturing[J]. Computers in biology and medicine, 2012, 42(5):548-555.
[9] VANDENBROUCKE B, KRUTH J P. Selective laser melting of biocompatible metals for rapid manufacturing of medical parts[J]. Rapid Prototyping Journal, 2007, 13(4):196-203.
[10] MEIER H, HABERLAND C. Experimental studies on selective laser melting of metallic parts[J]. Materialwissenschaft und Werkstofftechnik, 2008, 39(9):665-670.
[11] MUMTAZ K, HOPKINSON N. Top surface and side roughness of Inconel 625 parts processed using selective laser melting[J]. Rapid Prototyping Journal, 2009, 15(2):96-103.
[12] KRUTH J P, BADROSSAMAY M, YASA E, et al. Part and material properties in selective laser melting of metals[C]//Proceedings of the 16th International Symposium on Electromachining, 2010.
[13] 赵彦华. KMN钢压缩机叶片激光熔覆修复及后续加工特性研究[D]. 济南:山东大学, 2015. ZHAO Yanhua. Research on laser cladding repaired and subsequent processing characteristics of KMN steel compressor blade[D]. Jinan:Shandong University, 2015.