多轴应力状态下结构的蠕变变形分析是高温装备强度设计的理论基础。经典的Cocks-Ashby多轴蠕变孔洞长大模型及其简化模型存在着严苛的适用条件及局限性，仅适用于描述高温低应力环境下以晶间蠕变孔洞长大过程为材料蠕变损伤主要形式的蠕变变形行为。根据其简化解得到的用于单-多轴蠕变延性换算的多轴蠕变因子则存在着在低三轴应力度段给出的计算值较试验值偏小的问题。在基于WITCHMANN对该问题修正工作的基础上，通过合理的进一步优化，一个新的多轴蠕变因子被得出。将新修正因子应用在一个处于简化恒定应力场中的发动机热端叶片算例上，计算出恒载下叶片的等效多轴蠕变应变分布。有限元计算结果表明在叶片模型的叶根中部区域存在着较大的三轴应力度及较小的多轴蠕变因子，使得叶根中部原本应变不太明显的区域也产生了较大的等效多轴蠕变应变，导致叶片计算出的潜在失效面积较未经多轴蠕变因子修正前显著增加。
胡靖东
,
刘长军
,
轩福贞
. 基于Cocks-Ashby模型的多轴蠕变设计准则的局限性及其修正[J]. 机械工程学报, 2017
, 53(16)
: 141
-147
.
DOI: 10.3901/JME.2017.16.141
Structure analysis of creep deformation under multiaxial stress state is the theoretical basis of high temperature equipment design. The classic cavity growth theory(CGT) Cocks-Ashby multiaxial power-law creep model and its simplification have the limitation and strict applicable condition that is only suitable for modeling the creep behavior whose main damage mechanism is the grain boundary voids growth. The multiaxial creep factor, which serves as the conversion between uniaxial and multiaxial creep ductility, in the simplified model has the problem that the values in low triaxiality are lower than the experimental data. Based on WITCHTMANN's work that gives a simple modification of this problem, a new multiaxial creep factor is proposed to give a better modification. A blade model has been built in a simplified static stress field to calculate the equivalent multiaxial creep strain distribution. Results show that the mid zone of the blade root has a relatively large equivalent multiaxial creep deformation because of the relatively large triaxiality and relatively small multiaxial creep factor, leading to significant increase of the total potential failure area after correction by multiaxial creep factor.
[1] KASSNER M E. Fundamentals of creep in metals and Alloys[M]. Oxford:Butterworth-Heinemann, 2015.
[2] BAILEY R W. The utilization of creep test data in engineering design[J]. Proceedings of the Institution of Mechanical Engineers, 1935, 131(1):131-349.
[3] DORN J E. Some fundamental experiments on high temperature creep[J]. Journal of the Mechanics and Physics of Solids, 1955, 3(2):85-88.
[4] 宫建国,温建锋,轩福贞. 蠕变-疲劳载荷下高温结构的缺口效应研究进展[J]. 机械工程学报, 2015, 51(24):24-40. GONG Jianguo, WEN Jianfeng, XUAN Fuzhen. Research progress on notch effect of high temperature components under creep-fatigue loading[J]. Journal of Mechanical Engineering, 2015, 51(24):24-40.
[5] 武欣宇,赵姿贞,陈旭. 一种2.25Cr1MoV钢加氢反应设备蠕变疲劳寿命设计方法[J]. 机械工程学报, 2015, 51(6):51-57. WU Xinyu, ZHAO Zizhen, CHEN Xu. A design approach for creep fatigue evaluation of hydrogenation reactor made of 2.25Cr1MoV steel[J]. Journal of Mechanical Engineering, 2015, 51(6):51-57.
[6] 孙见忠,左洪福,梁坤. 基于民航发动机状态数据的涡轮叶片剩余寿命评估[J]. 机械工程学报, 2015, 51(23):53-59. SUN Jianzhong, ZUO Hongfu, LIANG Kun. Remaining useful life estimation method for the turbine blade of civil aircraft engine based on the QAR and field failure data[J]. Journal of Mechanical Engineering, 2015, 51(23):53-59.
[7] 庄法坤,涂善东,周帼彦,等. 不同小试样测量蠕变性能的比较研究[J]. 机械工程学报, 2015, 51(6):9-18. ZHUANG Fakun, TU Shantung, ZHOU Guoyan, et al. Comparative study on the determination of creep properties by using different types of small specimens[J]. Journal of Mechanical Engineering, 2015, 51(6):9-18.
[8] RIMMER D, HULL D E. The growth of grain-boundary voids under stress[J]. Philosophical Magazine, 1959, 4(42):673-687.
[9] NEEDLEMAN A, RICE J R. Plastic creep flow effects in the diffusive cavitation of grain boundaries[J]. Acta Metallurgica, 1980, 28(10):1315-1332.
[10] COCKS A C F, ASHBY M F. Intergranular fracture during power-law creep under multiaxial stresses[J]. Metal science, 1980, 14(8-9):395-402.
[11] COCKS A C F., ASHBY M F. Creep fracture by coupled power-law creep and diffusion under multiaxial stress[J]. Metal Science, 1982, 16(10):465-474.
[12] YAO H T, XUAN F Z, WANG Z D, et al. A review of creep analysis and design under multi-axial stress states[J]. Nuclear Engineering and Design, 2007, 237(18):1969-1986.
[13] MARTIN J B. Impulsive loading theorems for rigid-plastic continua[J]. Journal of the Engineering Mechanics Division, 1964, 90(5):27-42.
[14] MARTIN J B, SYMONDS P S. Mode approximations for impulsively-loaded rigid-plastic structures[J]. Journal of the Engineering Mechanics Division, 1966, 92(5):43-66.
[15] MCCLINTOCK F A, IRWIN G R. Plasticity aspects of fracture mechanics[M]. West Conshohocken:ASTM International, 1965.
[16] RICE J R, TRACEY D M. On the ductile enlargement of voids in triaxial stress fields[J]. Journal of the Mechanics and Physics of Solids, 1969, 17(3):201-217.
[17] WICHTMANN A. Creep and fatigue at elevated temperatures. evaluation of creep damage due to void growth under triaxial stress states in the design of steam turbine components[J]. JSME International Journal Series A Solid Mechanics and Material Engineering, 2002, 45(1):72-76.
[18] WEN J F, TU S T. A multiaxial creep-damage model for creep crack growth considering cavity growth and microcrack interaction[J]. Engineering Fracture Mechanics, 2014, 123:197-210.
[19] SPINDLER M W. The multiaxial creep ductility of austenitic stainless steels[J]. Fatigue and Fracture of Engineering Materials and Structures, 2004, 27(4):273-281.
[20] 梁浩宇,段滋华. 304不锈钢构件的高温蠕变特性分析[J]. 太原理工大学学报, 2013, 44(3):308-311. LIANG Haoyu, DUAN Zihua. High-temperature creep numerical simulation of 304 stainless steel component[J]. Journal of Taiyuan University of Technology, 2013, 44(3):308-311.