The wettability of the solder directly determines the performance of the solder joint in the field of microelectronic packaging soft soldering. In this work, the SAC305/Cu soldering system was employed as the research object, and on the premise that no foreign elements are added, and wetting tests of SAC305 solder on Cu substrates with different roughnesses were completed. The influence of Cu substrate roughness on the wettability of SnAgCu solder and the morphology and distribution of SnAgCu/Cu interface compounds is analyzed. The results show that the wetting angle of SnAgCu solder on the Cu substrate increases as the substrate roughness decreases, and when the substrate roughness decreases to a certain degree, the wetting angle no longer changes with the substrate roughness changing. The reaction between the SnAgCu solder and the Cu substrate produces the intermetallic compound Cu6Sn5. Cu6Sn5 grows perpendicular to the surface of the substrate in a scallop shape from the substrate to the solder direction. The thickness of the Cu6Sn5 layer first increases and then decreases with the decrease in roughness. And the Cu6Sn5 layer interdiffuses with the substrate and the solder layer.
ZHANG Zhihang
,
YANG Jian
,
YANG Zhen
,
HUANG Jihua
,
CHEN Shuhai
. Influence of Cu substrate roughness on wettability of SnAgCu lead-free solder[J]. Transactions of The China Welding Institution, 2022
, 43(1)
: 22
-28
.
DOI: 10.12073/j.hjxb.20210609002
[1] Gao S, Nan Z L, Li Y, et al. Copper matrix thermal conductive composites with low thermal expansion for electronic packaging[J]. Ceramics International, 2020, 46(11): 18019 - 18025.
[2] Warzoha R J, Wilson A A, Donovan B F, et al. Applications and impacts of nanoscale thermal transport in electronics packaging[J]. Journal of Electronic Packaging, 2021, 143(2): 020804.
[3] 王慧, 薛松柏, 陈文学, 等. Ag, Al, Ga对Sn-9Zn无铅钎料润湿性能的影响[J]. 焊接学报, 2007, 28(8): 33 - 36,44
Wang Hui, Xue Songbai, Chen Wenxue, et al. Influence of Ag, Al, Ga on the wettability of Sn-9Zn lead-free solder[J]. Transactions of China Welding Institution, 2007, 28(8): 33 - 36,44
[4] Wang C H, Kuo C Y, Guo Y B. Effects of minor Cu, Ni and Ag additions on the reactions between Sn-based solders and Co substrate[J]. JOM, 2019, 71(9): 3023 - 3030.
[5] Zhang M, Zhang K K, Huo F P, et al. Microstructures and properties of Sn2.5Ag0.7Cu0.1RE composite solders rein forced with Cu-coated graphene nanosheets synthesized by pyrolysis.[J]. Materials, 2019, 12(2): 289.
[6] Suganuma K. Advances in lead-free electronics soldering[J]. Current Opinion in Solid State and Materials Science, 2001, 5(1): 55 - 64.
[7] Kim K S, Huh S H, Suganuma K. Effects of fourth alloying additive on microstructures and tensile properties of Sn-Ag-Cu alloy and joints with Cu[J]. Microelectronics Reliability, 2003, 43(2): 259 - 267.
[8] 寇璐璐, 曲文卿, 庄鸿寿. 微量元素对Sn-3.5Ag-0.7Cu钎料性能的影响[J]. 航空制造技术, 2020, 63(8): 87 - 92
Kou Lulu, Qu Wenqing, Zhuang Hongshou. Effect of trace elements on the properties of Sn-3.5Ag-0.7Cu solder[J]. Aeronautical Manufacturing Technology, 2020, 63(8): 87 - 92
[9] 赵玉萍, 霍飞. 温度与镀层对Sn0.7Cu焊料合金润湿性的影响[J]. 有色金属材料与工程, 2015, 36(2): 65 - 70
Zhao Yuping, Huo Fei. Effect of temperature and coating on the wettability of Sn0.7Cu solder alloy[J]. Nonferrous Metal Materials and Engineering, 2015, 36(2): 65 - 70
[10] Tu K N, Zeng K. Tin-lead (SnPb) solder reaction in flip chip technology[J]. Materials Science and Engineering:R: Reports, 2001, 34(1): 1 - 58.
[11] Luo Y F, Deng Y L, Guan L Q, et al. Effect of grain size and crystal orientation on the corrosion behavior of as-extruded Mg-6Gd-2Y- 0.2Zr alloy[J]. Corrosion Science, 2020, 164: 108338.
[12] Zou H F, Yang H J, Zhang Z F. Morphologies, orientation relationships and evolution of Cu6Sn5 grains formed between molten Sn and Cu single crystals[J]. Acta Materialia, 2008, 56(11): 2649 - 2662.
[13] Suh J O, Tu K N, Tamura N. A synchrotron radiation X-ray microdiffraction study on orientation relationships between a Cu6Sn5 and Cu substrate in solder joints[J]. JOM, 2006, 58(6): 63 - 66.