Aiming at the failure to join for the constituent materials brass and 304 stainless steel using resistance soldering at high temperatures, due to the presence of a nylon component, welding experiments were conducted using low-temperature connection method of resistance soldering so as to achieve sealing effect. The results show that under the pressure 0.3 MPa and the welding current 26 kA, the joining with double-layer Sn-Pb foil as brazing filler is available, and the brass center nylon component is not damaged. Observed by scanning electron microscope, surface diffusion occurred between solder and stainless steel or brass. The results of sealing test in water show that the weld area is sealed and the waterproof effect is achieved.
SUN Zhichao
,
SANG Jian
,
SUI Yingjie
,
WANG Bo
,
ZHANG Hongtao
. Study on brass and 304 stainless steel packaging process by resistance soldering[J]. Transactions of The China Welding Institution, 2019
, 40(5)
: 137
-142
.
DOI: 10.12073/j.hjxb.2019400141
[1] 高振永.紫铜/黄铜焊接接头微观组织及力学性能研究[D].哈尔滨:哈尔滨工业大学, 2009.
[2] 管永星. 304不锈钢软钎焊用钎剂研究[D].南京:南京航空航天大学, 2013.
[3] 张志强,荆洪阳,徐连勇,等.双相不锈钢多层多道焊接接头微观组织表征[J].焊接学报, 2017(5):83-86 Zhang Zhiqiang, Jing Hongyang, Xu Lianyong, et al. Microstructural characterization of multi-phase stainless steel multi-layer welded joints[J]. Transactions of the China Welding Institution, 2017(5):83-86
[4] Yang Ke, Zhang Zhixi, Jiang Yongfeng, et al. Microstructure and corrosion resistance of 304 stainless steel electroslag strip cladding[J]. China Welding, 2016, 25(1):15-20.
[5] 宫文彪,毛亚芬,张秋征,等. H62黄铜搅拌摩擦焊接头微观结构及性能[J].焊接学报, 2014, 35(2):83-86 Gong Wenbiao, Mao Yafen, Zhang Qiuzheng, et al. Microstructure and properties of H62 brass friction stir welded joints[J]. Transactions of the China Welding Institution, 2014, 35(2):83-86
[6] Tasak E, Stankiewicz M, Gierlicki R, et al. Properties of joints welded in dissimilar materials[J]. Welding International, 2003, 17(4):293-297.
[7] Li G, Lu X F, Zhu X L, et al. Fiber laser butt joining of AZ31B alloy to 304 stainless steels with copper foil[J]. Optics and Laser Technology, 2019, 117:215-226.
[8] Shakhmatov M V, Shakhmatov D M. Features of resistance butt welding of cast iron[J]. Welding International, 2004, 18(9):737-741.
[9] Sidyakin V A, Danilov A I. Low-pressure arc butt welding of steel and nickel alloy pipes in power engineering[J]. Welding International, 2004, 18(4):324-329.
[10] Veselov V A. Butt welding with the heating by the low pressure arc of steel-aluminium pipe transition pieces for cryogenic systems and equipment[J]. Avt Svarka, 1990, 22(4):50-55.
[11] 林茂广,王海龙.奥氏体不锈钢与纯铜的真空钎焊工艺研究[J].热加工工艺, 2013, 42(9):176-178 Lin Maoguang, Wang Hailong. Research on vacuum brazing process of austenitic stainless steel and pure copper[J]. Thermal Engineering Technology, 2013, 42(9):176-178
[12] 郭红.铜与不锈钢的真空钎焊[D].武汉:武汉理工大学, 2003.
[13] Tosto S, Nenci F, Hu J, et al. Microstructure of copper-AISI type 304L electron beam welded alloy[J]. Materials Science and Technology, 2003, 19(4):519-522.
[14] Magnabosco I, Ferro P, Bonollo F, et al. An investigation of fusion zone microstructures in electron beam welding of copper-stainless steel[J]. Materials Science&Engineering A, 2006, 424(1-2):163-173.