The influence of welding thermal cycle parameters on the microstructure and impact property of the coarse grain zone in the HAZ of TiNb steel for large-line energy welding was studied by thermal simulation technology. The results show that the coarse-grained microstructure of the heat-affected zone of TiNb steel is mainly composed of bainite, ferrite and pearlite. When the peak temperature of thermal cycle increases, the content of pearlite and ferrite decreases, and the content of bainite increases, the slab structure is obviously roughened, resulting in the decrease of impact toughness, the prolonging of high temperature residence time, the reduction of bainite and pearlite content, and the increasing of polygonal ferrite content. The high-temperature ferrite structure is thick when the high temperature residence time is above 10 s. Then the impact toughness is drastically reduced. Under the appropriate cooling time conditions, the main microstructure is fine acicular ferrite structure, and the impact toughness reaches the maximum. With a lower thermal cycle peak temperature, a shorter high temperature residence time and a suitable cooling time, a fine grained ferrite structure can be obtained, which can significantly improve the impact toughness of the heat affected coarse grain zone.
FU Kuijun
,
GAO Mingze
,
LENG Xuesong
,
YAN Junchun
,
TANG Haoyang
. Evolution of microstructure and impact property in welding HAZ of TiNb steel[J]. Transactions of The China Welding Institution, 2019
, 40(5)
: 36
-41
.
DOI: 10.12073/j.hjxb.2019400124
[1] 廖建国.大线能量焊接用厚钢板的发展[J].宽厚板, 2002, 8(2):44-48 Liao Jianguo. Development in structural steel plates for high-heat input welding[J]. Lenient Plate, 2002, 8(2):44-48
[2] 习小军,赖朝彬,吴春红,等.大线能量焊接船板钢的研究现状与发展[J].有色金属科学与工程, 2016, 7(5):56-59 Xi Xiaojun, Lai Chaobin, Wu Chunhong, et al. Research situation and development of ship plate steel by high heat input welding[J]. Nonferrous Metals Science and Engineering, 2016, 7(5):56-59
[3] Bonnevie E, Ferrière G, Ikhlef A, et al. Morphological aspects of martensite-austenite constituents in intercritical and coarse grain heat affected zones of structural steels[J]. Material Science Engineering:A, 2004, 385(1-2):352-358.
[4] Zhang L, Kannengiesser T. Austenite grain growth and microstructure control in simulated heat affected zones of microalloyed HSLA steel[J]. Materials Science&Engineering A, 2014, 613:326-335.
[5] 李静,王华,曲圣昱,等.焊接热循环参数对大线能量焊接用钢EH40热影响区组织和性能的影响[J].北京科技大学学报, 2012, 34(7):788-792 Li Jing, Wang Hua, Qu Shengyu, et al. Effect of welding thermal cycle parameters on the microstructure and propertise in the heat affected zone of steel EH40 for high heat input welding[J]. Journal of University of Science and Technology Beijing, 2012, 34(7):788-792
[6] 宋峰雨,李艳梅,王平,等.大热输入焊接接头组织性能研究[J].内蒙古工业大学学报, 2017, 36(1):6-9 Song Fengyu, Li Yanmei, Wang Ping, et al. Study on micostructure properties of welded joints with high heat input welding[J]. Journal of Inner Monuolia University of Technology, 2017, 36(1):6-9
[7] 徐学利,辛希贤,石凯,等.焊接热循环对X80管线钢粗晶区韧性和组织的影响[J].焊接学报, 2005, 26(8):69-72 Xu Xueli, Xin Xixian, Shi Kai. Influence of welding thermal cycle on toughness and microstructure in grain-coarsening region of X80 pipeline steel[J]. Transaction of the China Welding Institute, 2005, 26(8):69-72
[8] 胡传顺,顾玉熹.热循环峰值温度对HQ100钢热影响区组织和性能的影响[J].金属热处理, 1999, 11:11-13 Hu Chuanshun, Gu Yuxi. Effect of thermal cycle peak temperature on microstructure and properties of heat affected zone of HQ100 Steel[J]. Metal Heat Treatment, 1999, 11:11-13
[9] Zhang L P, Davis C L, Strang W M. Effect of TiN particles and microstructures on fracture toughness in simulated heat-affected-zones of a structural steel[J]. Metallurgical and Material Transactions, 1999, 30A (8):2089-2096.
[10] 赵琳,张旭东,陈武柱. 800MPa级低合金钢焊接热影响区韧性的研究[J].金属学报, 2015, 41(4):392-393 Zhao Lin, Zhang Xudong, Chen Wuzhu. Toughness of heat-affected zone of 800 MPa grade low alloy steel[J]. Acta Metallurgica Sinica, 2015, 41(4):392-393