The current research of narrow-gap gas metal arc welding (NG-GMAW) primarily focuses on improving the sidewall fusion and avoiding the lack-of-fusion defect. However, the high cost and operation difficulty of the methods limit the industrial application. In this study, small amount of active gases CO2 and O2 were added into pure argon inert shielding gas to improve the weld formation of pulsed-current narrow-gap gas metal arc welding (NG-GMAW) of mild steel. Their effects on droplet transfer and arc behavior were investigated. A high-speed visual sensing system was utilized to observe the metal transfer process and arc morphology. When the proportion of CO2, being added into the pure argon shielding gas, changes from 5% to 25%, the metal transfer mode changes from pulsed spray streaming transfer to pulsed projected spray transfer, while it remains the pulsed spray streaming transfer when 2% to 10% O2 is added. Both CO2 and O2 are favorable to stabilizing arc and welding process. O2 is even more effective than CO2. However, O2 is more likely to cause slags on the weld surface, while CO2 can improve the weld appearance in some sense. The weld surface concavity in NG-GMAW is greatly influenced by the addition of active gas, but the weld width and weld penetration almost keep constant. This study proposes a new method which is beneficial to improving the weld bead formation and welding process stability.
[1] C X Zhu, X H Tang, Y He, et al. Effect of preheating on the defects and microstructure in NG-GMA welding of 5083 Al-alloy. Journal of Materials Processing Technology, 2018, 251: 214-224.
[2] G X Xu, L Li, J Y Wang, et al. Study of weld formation in swing arc narrow gap vertical GMA welding by numerical modeling and experiment. The International Journal of Advanced Manufacturing Technology, 2018, 96(5-8): 1905-1917.
[3] C X Zhu, X H Tang, Y He, et al. Study on arc characteristics and their influences on weld bead geometry in narrow gap GMAW of 5083 Al-alloy. The International Journal of Advanced Manufacturing Technology, 2017, 90(9-12): 2513-2525.
[4] Y He, X H Tang, C X Zhu, et al. Study on insufficient fusion of NG-GMAW for 5083 Al alloy. The International Journal of Advanced Manufacturing Technology, 2017, 92(9-12): 4303-4313.
[5] C X Zhu, J Cheon, X H Tang, et al. Effect of swing arc on molten pool behaviors in narrow-gap GMAW of 5083 Al-alloy. Journal of Materials Processing Technology, 2018, 259: 243-258.
[6] B Duan, J C Wang, Z H Lu, et al. Parameter analysis and optimization of the rotating Arc NG-GMAW welding process. International Journal of Simulation Modelling, 2018, 17(1): 170-179.
[7] J F Wang, Q J Sun, T Zhang, et al. Arc characteristics in alternating magnetic field assisted narrow gap pulsed GTAW. Journal of Materials Processing Technology, 2018, 54: 254-264.
[8] Y F Meng, G Li, M Gao, et al. Formation and suppression mechanism of lack of fusion in narrow gap laser-arc hybrid welding. The International Journal of Advanced Manufacturing Technology, 2019, 100(9-12): 2299-2309.
[9] Y F Meng, G Li, M Gao, et al. Effects of groove parameters on space constraint of narrow gap laser-arc hybrid welding. Journal of Manufacturing Processes, 2018, 33: 144-149.
[10] X Y Cai, C L Fan, S B Lin, et al. Effects of shielding gas composition on arc characteristics and droplet transfer in tandem narrow gap GMA welding. Science and Technology of Welding and Joining, 2017, 22(5): 446-453.
[11] G Q Liu, X H Tang, S Y Han, et al. Influence of interwire angle on undercutting formation and arc behavior in pulsed tandem narrow-gap GMAW. Materials & Design, 2020, 193: 108795.
[12] A Aoki, S Tashiro, H Kurokawa, et al. Development of novel MIG welding process with duplex current feeding. Journal of Manufacturing Processes, 2019, 47: 74-82.
[13] S W Zhang, J H Sun, M H Zhu, et al. Effects of shielding gases on process stability of 10CrNi3MoV steel in hybrid laser-arc welding. Journal of Materials Processing Technology, 2019, 270: 37-46.
[14] H Y Huang. Effects of shielding gas composition and activating flux on GTAW weldments. Materials and Design, 2009, 30: 2404-2409.
[15] J H Sun, P L Nie, K Feng, et al. The elimination of pores in laser welds of AISI 304 plate using different shielding gases. Journal of Materials Processing Technology, 2017, 248: 56-63.
[16] R Zong, J Chen, C S Wu, et al. Influence of shielding gas on undercutting formation in gas metal arc welding. Journal of Materials Processing Technology, 2016, 234: 169-176.
[17] P Jonsson, A B Murphy, J Szekely. The influence of O2 additions on argon-shielded gas metal arc welding processes. Welding Journal-Including Welding Research Supplement, 1995, 74(2): 48s.
[18] L L Wang, F G Lu, H P Wang, et al. Effects of shielding gas composition on arc profile and molten pool dynamics in gas metal arc welding of steels. Journal of Physics D: Applied Physics, 2014, 47(46): 465202.
[19] S Chandra-ambhorn, P Saranyachot. Effect of the H2 content in shielding gas on the microstructure and oxidation resistance of Fe?15.7 wt. % Cr?8.5 wt. % Mn steel GTA welds. Journal of Materials Processing Technology, 2019, 268: 18–24.
[20] X Y Cai, C L Fan, S B Lin, et al. Effects of shielding gas composition on arc behaviors and weld formation in narrow gap tandem GMAW. The International Journal of Advanced Manufacturing Technology, 2017, 91: 3449-3456.
[21] Y Zhao, X J Shi, K Yan, et al. Effect of shielding gas on the metal transfer and weld morphology in pulsed current MAG welding of carbon steel. Journal of Materials Processing Technology, 2018, 262: 382-391.
[22] Y R Wong, S F Ling. An investigation of dynamical metal transfer in GMAW—Effects of argon shielding gas. Journal of Materials Processing Technology, 2014, 214: 106-111.
[23] A B Murphy, C J Arundelli. Transport coefficients of argon, nitrogen, oxygen, argon-nitrogen, and argon-oxygen plasmas. Plasma Chemistry and Plasma Processing, 1994, 14(4): 451-490.
[24] V A Nemchinsky. Size and shape of the liquid droplet at the molten tip of an arc electrode. Journal of Physics D: Applied Physics, 1994, 27(7): 1433.
[25] A Scotti, V Ponomarev, W Lucas. A scientific application oriented classification for metal transfer modes in GMA welding. Journal of Materials Processing Technology, 2012, 212(6): 1406-1413.
[26] Y S Kim, T W Eagar. Analysis of metal transfer in gas metal arc welding. Welding Journal- New York, 1993, 72(6): 269s–278s.
[27] P Sahoo, T Debroy, M J McNallan. Surface tension of binary metal-surface active solute systems under conditions relevant to welding metallurgy. Metallurgical transactions B, 1988, 19(3): 483-491.
[28] S Rhee, E Kannatey-Asibu. Observation of metal transfer during gas metal arc welding. Welding Journal- New York, 1992, 71: 381-386.
[29] J C Amson. Lorentz force in the molten tip of an arc electrode. British Journal of Applied Physics, 1965, 16(8): 1169.
[30] J Chen, C S Wu. Numerical analysis of forming mechanism of hump bead in high speed GMAW. Welding in the World, 2010, 54(9-10): 286-291.
[31] H G Fan, Y W Shi. Numerical simulation of the arc pressure in gas tungsten arc welding. Journal of Materials Processing Technology, 1996, 61(3): 302-308.