A printed circuit board of remote controller occurred corrosion failure. The corrosion failure causes of the circuit board were analyzed by means of macroscopic analysis, scanning electron microscopy analysis, energy spectrum analysis and infrared analysis. The results show that the tin coating in some places of the circuit board of remote controller were missing in the manufacturing process, which lost the protective effect on the substrate, and the substrate occurred oxidation corrosion. The tin coating in some places had high impurity content. With the participation of water vapor, oxygen, carbon dioxide and acid mist in the atmosphere, tin, as the negative electrode of galvanic cell corroded under thin liquid film, lost electrons and occurred electrochemical corrosion. Under the combined action of two kinds of corrosion, the circuit board of remote controller corrosion failure was eventually caused.
HU Lifen
,
WANG Shanshan
. Corrosion Failure Causes of Printed Circuit Board of Remote Controller[J]. Physical Testing and Chemical Analysis Part A:Physical Testing, 2020
, 56(12)
: 71
-73
.
DOI: 10.11973/lhjy-wl202012017
[1] 林金堵. 现代印制电路基础[M].上海:印制电路信息杂志社,2001.
[2] 杨振国.印制电路板的失效分析[J].金属热处理,2011,3(增刊):5-6.
[3] 陶剑磊,方培源,王家辑,等.由版图引起的CMOS ESD保护电路失效分析[J].半导体技术,2007,32(11):1003-1006.
[4] 王东柱,李明.电除尘器极线腐蚀失效原因分析[J].理化检验(物理分册),2017,53(3):201-204.
[5] 魏亮新,黄子东,洪泽浩,等.304不锈钢防盗罩锈蚀原因分析[J].理化检验(物理分册),2018,54(5):378-381.
[6] 郝文魁,杨丙坤,马光,等.沿海工业环境下6A02铝合金接线板的腐蚀行为[J].机械工程材料,2017,41(12):59-63.
[7] 宁文涛,冯皓,赵越.印刷线路板在复合环境下的腐蚀[J].环境适应性和可靠性,2010,31(6):30-32.