High-speed steel is a kind of special tool steel with high hardness and wear resistance. The microhardness loss of high-speed steel that is subjected to spheroidizing annealing is large, which significantly affects its application. In order to increase the microhardness of spheroidal annealing W6Mo5Cr4V2 high-speed steel surface, and to ensure its good internal toughness, the electron beam surface remelting is used to harden the surface. The remelting surface is flat and smooth with small craters. Cellular dendrites are observed in the remelting layer, which is mainly composed of martensite, residual austenite, M2C eutectic carbide, and fine rod-shaped MC carbide, the formation process and types of intercrystalline carbides are analyzed. After electron beam surface remelting, the microhardness of the W6Mo5Cr4V2 high-speed steel surface is increased from 283 HV to more than 800 HV, indicating the prominent recovery effect of microhardness.
CHEN Guoqing
,
TEN Xinyan
,
SHU Xi
,
ZHANG Binggang
. Hardening effect of electron beam surface remelting on W6 steel[J]. Transactions of The China Welding Institution, 2021
, 42(12)
: 1
-6
.
DOI: 10.12073/j.hjxb.20210413002
[1] 李远波, 吴德成, 刘国跃, 等. 焊接电流对M51/B318异种金属精密电阻焊接头质量的影响[J]. 焊接学报, 2019, 40(5): 73 ? 78
Li Yuanbo, Wu Decheng, Liu Guoyue, et al. Effect of welding current on welding quality of M51/B318 dissimilar metal joint using resistance welding[J]. Transactions of the China Welding Institution, 2019, 40(5): 73 ? 78
[2] Zhou X F, Fang F, Jiang J Q, et al. Refining carbide dimensions in AISI M2 high speed steel by increasing solidification rates and spheroidising heat treatment[J]. Materials Science and Technology, 2014, 30(1): 116 ? 122.
[3] Yan X G, Li D Y. Effects of the sub-zero treatment condition on microstructure, mechanical behavior and wear resistance of W9Mo3Cr4V high speed steel[J]. Wear, 2013, 302(1?2): 854 ? 862.
[4] Dhokey N B, Hake A, Kadu S, et al. Influence of cryoprocessing on mechanism of carbide development in cobalt-bearing high-speed teel (M35)[J]. Metallurgical and Materials Transactions A, 2014, 45(3): 1508 ? 1516.
[5] Zhang Guoqing, Yuan Hua, Jiao Dongling, et al. Microstructure evolution and mechanical properties of T15 high speed steel prepared by twin-atomiser spray forming and thermo-mechanical processing[J]. Materials Science & Engineering A, 2012, 558: 566 ? 571.
[6] Ma Liping, Zhao Wenxiang, Liang Zhiqiang, et al. An investigation on the mechanical property changing mechanism of high speed steel by pulsed magnetic treatment[J]. Materials Science & Engineering A, 2014, 609: 16 ? 25.
[7] 秦宇飞, 刘剑, 罗湘燕. 热处理对低合金高速钢碳化物的影响[J]. 材料热处理技术, 2010, 24: 216 ? 219
Qin Yufei, Liu Jian, Luo Xiangyan. Effect of heat treatment on carbide in low alloy high speed steel[J]. Material & Heat Treatment, 2010, 24: 216 ? 219
[8] Yin Yan, Kang Ping, Zhang Ruihua, et al. Effect of heat treatment on microstructure and properties of VG10 and 3Cr13 dissimilar welded joints[J]. China Welding, 2021, 30(1): 21 ? 29.
[9] Jisoo Kim, Jin-Seok Kim, Eun-Goo Kang, et al. Surface modification of the metal plates using continuous electron beam process (CEBP)[J]. Applied Surface Science, 2014, 311: 201 ? 207.
[10] Hao S, Gao B, Wu A, et al. Surface modification of steels and magnesium alloy by high current pulsed electron beam[J]. Nuclear Instruments & Methods in Physics Research Section B-Bear Intercations with Materials and Atoms, 2005, 240: 646 ? 652.
[11] 魏德强, 李新凯, 任旭隆. 电子束表面改性研究进展[J]. 热加工工艺, 2016, 45: 19 ? 23
Wei Deqiang, Li Xinkai, Ren Xulong. Research progress on surface modification of electron beam[J]. Hot Working Technology, 2016, 45: 19 ? 23
[12] 李玉海, 肖福仁, 王玉辉, 等. 强流脉冲离子束辐照对M2高速钢的表面改性[J]. 材料研究学报, 2005, 19: 55 ? 60
Li Yuhai, Xiao Furen, Wang Yuhui, et al. M2 high speed steel irradiated by high-intensity pulsed ion beam[J]. Chinese Journal of Materials Research, 2005, 19: 55 ? 60
[13] 章为夷. 等温球化处理过程中球状碳化物的Ostwald长大现象[J]. 材料科学与工艺, 1993, 1: 44 ? 48
Zhang Weiyi. Ostwald Repening of spherical carbide during isothermal spheroidizing[J]. Material Science & Technology, 1993, 1: 44 ? 48
[14] Zhang Li, Chen Shu, Wang Yuan jie, et al. Tungsten carbide platelet-containing cemented carbide with yttrium containing dispersed phase[J]. Transactions of Nonferrous Metals Society of China, 2008, 18(1): 104 ? 108.
[15] Wang H, Hou L, Zhang J, et al. The secondary precipitates of niobium-alloyed M3: 2 high speed steel prepared by spray deposition[J]. Mater Charact, 2015, 106: 245 ? 254.
[16] Qu M, Wang Z, Li H, et al. Effects of mischmetal addition on phase transformation and as-cast microstructure characteristics of M2 high-speed steel[J]. J Rare Earth, 2013, 31: 628 ? 633.
[17] Chen G, Yin Q, Zhang G, et al. Underlying causes of strength weakening of electron beam welded joints of high-speed steels[J]. J Manuf Process, 2019, 39: 250 ? 258.