A semi-solid brazing process assisted by magnetic pulse for steel/aluminum tube was proposed by combining electromagnetic forming technology and semi-solid brazing technology. The brazing of steel and aluminum dissimilar pipes without flux soldering was realized by means of the radial compression and axial shear action of solid particles in the semi-solid solder to remove the oxide film on the surface of the base metal. The diffusion behavior of interface elements and the growth mechanism of intermetallic compounds in brazing joints were studied by magnetic pulse semi-solid brazing experiments of steel/aluminum tubes under different process parameters. The results show that the weld microstructure is mainly composed of α-Al and zinc-rich phase. The Al2O3 oxide film at the aluminum side interface is broken and removed well, and a thin layer of FeAl3 intermetallic compound is formed at the steel side interface. Good metallurgical bonding is achieved at all parts.
YANG Zheng
,
HU Jianhua
,
WANG Yueshen
,
YANG Lingzhi
. Interface behavior of steel/Al tube assisted semi-solid brazing by magnetic pulse[J]. Transactions of The China Welding Institution, 2021
, 42(11)
: 51
-56
.
DOI: 10.12073/j.hjxb.20201217002
[1] Tisza M, Czinege M. Comparative study of the application of steels and aluminium in lightweight production of automotive parts[J]. International Journal of Lightweight Materials and Manufacture, 2018, 1(4): 229 ? 238.
[2] 吴杰, 薛松柏, 费文潘, 等. 铝/钢异种材料钎焊研究现状与发展趋势[J]. 材料导报, 2019, 33(21): 3533 ? 3540
Wu Jie, Xue Songbai, Fei Wenpan, et al. Research status and development trend of aluminum/steel dissimilar material brazing[J]. Materials Guide, 2019, 33(21): 3533 ? 3540
[3] Cheepu M, Che W S. Friction welding of titanium to stainless steel using Al interlayer[J]. Transactions of the Indian Institute of Metals, 2019, 72(6): 1563 ? 1568.
[4] Zhang Changqing, Lü Guangming, Jin Xin, et al. Study of joining mechanism of ABS polymer and steel/aluminum by resistance spot welding[J]. China Welding, 2018, 27(2): 57 ? 62.
[5] 邱哲睿, 邓永芳, 刘赣华, 等. 铝/钢异种材料搅拌摩擦焊接研究现状及发展[J]. 特种铸造及有色合金, 2020, 40(5): 512 ? 518
Qiu Zherui, Deng Yongfang, Liu Ganhua, et al. Research status and development of friction stir welding of aluminum / steel dissimilar materials[J]. Special Casting and Nonferrous Alloy, 2020, 40(5): 512 ? 518
[6] Matteis A, Gullino F, Aiuto C, et al. Welding between aluminum alloy and steel sheets by using transition joints[J]. Journal of Materials Engineering and Performance, 2020, 29(8): 4840 ? 4853.
[7] Schubert E, Klassen M, Zerner I, et al. Light-weight structures produced by laser beam joining for future applications in automobile and aerospace industry[J]. Journal of Materials Processing Technology, 2001, 115(1): 2 ? 8.
[8] 高远. 铜铝异种金属管磁脉冲-半固态复合辅助钎焊温度条件研究[D]. 武汉: 武汉理工大学, 2019.
Gao Yuan. Study on temperature conditions of magnetic pulse-semi-solid composite assisted brazing of copper and aluminum dissimilar metal tubes[D]. Wuhan: Wuhan University of Technology, 2019.
[9] 崔佃忠, 芦笙, 崔晴晴, 等. 焊接热输入对铝/镀锌钢CMT熔-钎焊接头组织与性能的影响[J]. 焊接学报, 2014, 35(9): 82 ? 86
Cui Dianzhong, Lu Sheng, Cui Qingqing, et al. Effect of heat input on microstructure and mechanical properties of CMT welding-brazing joint between 5052 aluminum alloy and galvanized Q235 steel[J]. Thansactions of the China Welding Institution, 2014, 35(9): 82 ? 86
[10] 张满, 张军, 蒋腾, 等. Fe-Al金属间化合物对铝/钢钎焊接头力学性能的影响[J]. 焊接学报, 2018, 39(1): 61 ? 64
Zhang Man, Zhang Jun, Jiang Teng, et al. Effect of Fe-Al intermetallic compound on mechanical property of aluminum/steel brazed joint[J]. Thansactions of the China Welding Institution, 2018, 39(1): 61 ? 64
[11] Agudo L, Eyidi D, Schmaranzer C H, et al. Intermetallic Fe xAl y-phases in a steel/Al-alloy fusion weld[J]. Journal of Materials Science, 2007, 42(12): 4205 ? 4214.
[12] Peyre P, Sierra G, Deschaux-Beaume F, et al. Generation of aluminium–steel joints with laser- induced reactive wetting[J]. Materials Science & Engineering A, 2007, 444(1-2): 327 ? 338.
[13] 黄健康, 何翠翠, 石玗, 等. 铝/钢异种金属焊接接头界面Al-Fe金属间化合物生成及其热力学分析[J]. 吉林大学学报(工学版), 2014, 44(4): 1037 ? 1041
Huang Jiankang, He Cuicui, Shi Yu, et al. Formation and thermodynamic analysis of Al Fe intermetallic compound at the interface of aluminum / steel dissimilar metal welded joint[J]. Journal of Jilin University(Engineering and Technology Edition), 2014, 44(4): 1037 ? 1041
[14] 陈云, 包晔峰, 蒋永锋. 铁铝焊接界面组织与性能的研究[J]. 材料开发与应用, 2010, 25(2): 34 ? 36
Chen Yun, Bao Yefeng, Jiang Yongfeng. Research on the microstructure and properties of iron-aluminum welding interface[J]. Material Development and Application, 2010, 25(2): 34 ? 36