In this paper, steel and tungsten were successfully bonded using hot isostatic pressing diffusion bonding with V/Nb composite interlayer. The interface structure and shear strength of the joints under high temperature-low pressure process (1 050 ℃, 20 MPa) and low temperature-high pressure process (950 ℃, 100 MPa) were investigated separately. The results show that the joints under high temperature-low pressure process and low temperature-high pressure process both have a W/Nb/V/steel four-layer structure and the shear strengths of the joints are 96.9 MPa and 104.2 MPa respectively. The fracture of the joints all appears at the Nb/V interfaces with no obvious chemical reaction. Compared with the joint under high temperature-low pressure process, reducing the bonding temperature and increasing the bonding pressure will benefit to form a dense joint, but will not promote the diffusion of elements at the weak interface (Nb/V) and significantly increase the shear strength of the joint.
CHEN Shuai
,
WANG Yue
,
YANG Jian
,
HUANG jihua
,
CHEN Shuhai
. Microstructure and properties of hot isostatic pressing diffusion bonding steel/tungsten joint with V/Nb composite interlayer[J]. Transactions of The China Welding Institution, 2020
, 41(11)
: 47
-53
.
DOI: 10.12073/j.hjxb.20200118001
[1] Wang M, Chen Y, Li X, et al. Effect of Cu interlayer on the microstructure and strength for brazing of tungsten/316L steel[J]. Journal of Materials Engineering and Performance, 2019, 28(3): 1-8.
[2] Wang J C, Wang W, Wei R, et al. Effect of Ti interlayer on the bonding quality of W and steel HIP joint[J]. Journal of Nuclear Materials, 2017, 485: 8-14.
[3] Jung Y I, Park J Y, Choi B K, et al. Fabrication of W/FMS joint mock-ups using a hot isostatic pressing[J]. Fusion Engineering and Design, 2014, 89(7-8): 1029-1032.
[4] Liu W S, Wang Z, Ma Y Z, et al. Investigation of tungsten/steel brazing using Ta and Cu interlayer[J]. Fusion Engineering and Design, 2016, 113: 102-108.
[5] Liu W S, Pang H K, Cai Q C, et al. Fabrication of W/steel joint using hot isostatic pressing with Ti/Cu/Ti liquid forming interlayer[J]. Fusion Engineering and Design, 2018, 135: 59-66.
[6] Jung Y, Park J Y, Choi B K, et al. Interfacial microstructures of HIP joined W and ferritic–martensitic steel with Ti interlayers[J]. Fusion Engineering and Design, 2013, 88: 2457-2460.
[7] Zhong Z, Jung H C, Hinoki T, et al. Effect of joining temperature on the microstructure and strength of tungsten/ferritic steel joints diffusion bonded with a nickel interlayer[J]. Journal of Materials Processing Technology, 2010, 210(13): 1805-1810.
[8] Basuki W W, Aktaa J. Investigation of tungsten/EUROFER97 diffusion bonding using Nb interlayer[J]. Fusion Engineering & Design, 2011, 86(9-11): 2585-2588.
[9] 冀小强, 李树杰, 马天宇, 等. 用Zr/Nb复合中间层连接SiC陶瓷与Ni基高温合金[J]. 硅酸盐学报, 2002, 30: 305-310
Ji Xiaoqiang, Li Shujie, Ma Tianyu, et al. Bonding SiC ceramics and Ni-based superalloys with Zr/Nb composite interlayer[J]. Journal of the Chinese Ceramic Society, 2002, 30: 305-310
[10] 张博. 金属元素热膨胀系数的评估与计算[D]. 湘潭: 湘潭大学, 2014.
Zhang Bo. Evaluation and calculation of thermal expansion coefficient of metallic elements[D]. Xiangtan: Xiangtan University, 2014.
[11] Wang Y, Yang J, Huang J, et al. Hot isostatic diffusion bonding tungsten alloy and high-strength steel Part I: Design and preparation of Ni-Si-B interlayer by magnetron sputtering[J]. Journal of Manufacturing Processes, 2018, 35: 360-367.
[12] Zhang J M, Li S X, Yang Z G, et al. Influence of inclusion size on fatigue behavior of high strength steels in the gigacycle fatigue regime[J]. International Journal of Fatigue, 2007, 29(4): 765-767.