The Ag-Cu-Ti filler metal was wetted on C/C composites by the TIG arc directly. The macroscopic features of the wetting filler metal under different holding times were observed. Besides, the microstructure and element distribution of the joints was analyzed by SEM and EDS, respectively. The experimental results showed that the filler metal can soften under certain holding time. When the holding time was 60 min, the wetting effect of filler metal on C/C composites was the best. The distribution of the TiC reaction layer was the most uniform and dense with a thickness of 1.3 μm. Besides, the maximum thickness of the diffusion layer was 5.5 μm. When the content of copper and silver in the filler metal approaching to the reaction interface remained the same, there were brittle compounds such as AgTi/CuTi3/Cu4Ti3. Meanwhile, Ti elements gathered near the interface and Ti2Cu was produced in the aggregation area.
YU Jiang
,
LIU Haoran
,
ZHAO Shuaitongze
,
YANG Xiao
,
ZHANG Wenjie
. Wettability of Ag-Cu-Ti filler metal on C/C composites under TIG arc[J]. Transactions of The China Welding Institution, 2020
, 41(9)
: 69
-73
.
DOI: 10.12073/j.hjxb.20191023002
[1] 张丽霞, 田成龙, 田晓羽, 等. 具有铼涂层的C/C复合材料与铌的真空钎焊[J]. 焊接学报, 2015, 36(12): 51 - 54
Zhang Lixia, Tian Chenglong, Tian Xiaoyu, et al. Research on vacuum brazing of C/C-Re composite to Nb[J]. Transactions of the China Welding Institution, 2015, 36(12): 51 - 54
[2] 冯贞伟, 高腾飞, 邵天威, 等. C/C复合材料与镍基高温合金GH3128钎焊[J]. 焊接学报, 2015, 36(12): 109 - 112
Feng Zhenwei, Gao Tengfei, Shao Tianwei, et al. Brazing of C/C composite and Ni-based high temperature alloy GH3128[J]. Transactions of the China Welding Institution, 2015, 36(12): 109 - 112
[3] Sun Zhan, Zhang Lixia, Zhang Bo, et al. A strategy to fabricate strength-ductility enhanced braze filler reinforced by 3-dimensional graphene sponge for joining C/C composites[J]. Materials & Design, 2020, 189: 108515.
[4] 曹健, 贺宗晶, 亓钧雷, 等. 采用(Ti/Si/Cu)f多层箔钎焊C/C复合材料与TiAl合金[J]. 机械工程学报, 2018, 254(9): 108 - 114
Cao Jian, He Zongjing, Qi Junlei, et al. Brazing of C/C composite to TiAl alloy using (Ti/Ni/Cu)f mulTi-foil filler[J]. Journal of Mechanical Engineering, 2018, 254(9): 108 - 114
[5] Liu Duo, Song Yanyu, Zhou Yinghao, et al. Brazing of C/C composite and Ti-6Al-4V with graphene strengthened AgCuTi filler: Effects of graphene on wettability, microstructure and mechanical properties[J]. Chinese Journal of Aeronautics, 2018, 31(7): 1602 - 1608.
[6] Chen Bo, Xiong Huaping, Mao Wei, et al. Wettability and interfacial reactions of PdNi-based brazing fillers on C-C composite[J]. Transactions of Nonferrous Metals Society of China, 2010, 20(2): 223 - 226.
[7] Zhao Yixuan, Song Xiaoguo, Tan Caiwang, et al. Microstructural evolution of Si3N4 /Ti6Al4V joints brazed with nano-Si3N4 reinforced AgCuTi composite filler[J]. Vacuum, 2017, 42: 58 - 65.
[8] Zhang Kexiang, Zhao Wenke, Zhang Fuqin, et al. New wetting mechanism induced by the effect of Ag on the interaction between resin carbon and AgCuTi brazing alloy[J]. Materials Science & Engineering A, 2017, 696: 216 - 219.
[9] Nomura M, Ichimori T, Iwamoto C, et al. Structure of wetting front in the Ag-Cu-Ti/SiC reactive system[J]. Journal of Materials Science, 2000, 35(16): 3953 - 3958.
[10] 王毅, 雷凯, 董文, 等. Ti对Ag-Cu系活性钎料微观组织及性能的影响[J]. 长春工程学院学报, 2013, 14(1): 34 - 38
Wang Yi, Lei Kai, Dong Wen, et al. The influence of Ti on microstructure and properties of Ag-Cu system active filler metal[J]. Journal of Changchun Institute of Technology, 2013, 14(1): 34 - 38
[11] 黄超, 林铁松, 何鹏, 等. TiBW/TC4钛合金与C/C复合材料钎焊头的界面组织结构[J]. 焊接学报, 2011, 32(7): 39 - 42
Huang Chao, Lin Tiesong, He Peng, et al. Microstructure of TiBW/TC4 alloy and C/C composite brazed joint[J]. Transactions of the China Welding Institution, 2011, 32(7): 39 - 42
[12] 王庆娟, 徐长征, 郑茂盛. 高性能Cu-Cr-Ag合金的软化性能[J]. 特种铸造及有色合金, 2006, 26(11): 691 - 693
Wang Qingjuan, Xu Changzheng, Zheng Maosheng. Soften behaviors of Cu-Cr-Ag alloy with high performance[J]. Special Casting & Nonferrous Alloys, 2006, 26(11): 691 - 693