The K-TIG welding technology was used to weld the 10 mm thick Q235 steel. The results showed that the welding process was stable, and the welded joint with good weld formation and no defects such as cracks and pores was obtained. The dynamic behavior of keyhole in the welding process was observed by high-speed photography test, and the microstructure and hardness of the welded joint were studied The mechanical properties such as tensile, impact and bending are tested. The results show that the stability of keyhole of K-TIG welding can be increased by improving the heat dissipation condition and reasonable assembly clearance; the Vickers hardness of weld area and heat affected area are higher than that of base metal; the tensile strength and impact toughness of welded joint are better than that of base metal; the weld area is mainly composed of fine acicular ferrite and a small amount of massive ferrite The K-TIG welding joint with excellent properties has been obtained, which has reference significance for the further study of K-TIG welding process of low carbon steel.
XU Liang
,
OUYANG Kai
,
YANG Haifeng
. Study on K-TIG welding process and properties of Q235 steel[J]. Transactions of The China Welding Institution, 2020
, 41(8)
: 68
-72
.
DOI: 10.12073/j.hjxb.20200603001
[1] Jarvis B L, Ahmed N U. Development of keyhole mode gas tungsten arc welding process[J]. Science & Technology of Welding & Joining, 2000, 5(1): 21 - 28.
[2] Lathabai S, Jarvis B L, Barton K J. Comparison of keyhole and conventional gas tungsten arc welds in commercially pure titanium[J]. Materials Science & Engineering A, 2001, 299(1): 81 - 93.
[3] Lathabai S, Jarvis B L, Barton K J. Keyhole gas tungsten arc welding of commercially pure zirconium[J]. Science & Technology of Welding & Joining, 2008, 13(6): 573 - 581.
[4] Cui S L, Liu Z M, Fang Y X, et al. Keyhole process in K-TIG welding on 4 mm thick 304 stainless steel[J]. Journal of Materials Processing Technology, 2017, 243: 217 - 228.
[5] Feng Y, Luo Z, Liu Z, et al. Keyhole gas tungsten arc welding ofAISI 316L stainless steel[J]. Materials & Design, 2015, 85: 24 - 31.
[6] Fang Y X, Liu Z M, Cui S L, et al. Improving Q345 weld microstructure and mechanical properties with high frequency current arc in keyhole mode TIG welding[J]. Journal of Materials Processing Technology, 2017, 250: 280 - 288.
[7] 柳阳, 王秋平. 保护气对304N不锈钢K-TIG焊接头组织性能的影响[J]. 焊接, 2017(9): 45 - 48
Liu Yang, Wang Qiuping. Influence of shielding gas on microstructure and properties of K-TIG welded 304N stainless steel[J]. Welding & Joining, 2017(9): 45 - 48
[8] 冯悦峤. 中厚钢板的深熔TIG焊工艺研究及温度场数值模拟[D]. 天津 天津大学, 2016.
Feng Yueqiao.Process investigation and temperature field simulation on deep penetration TIG welding of mid- thickness steel[D]. Tianjin: Tianjin University, 2016.
[9] 韩涛, 谷世伟, 徐良, 等. K-TIG 焊接接头的应力与变形[J]. 焊接学报, 2019, 40(11): 125 - 132
Han Tao, Gu Shiwei, Xu Liang, et al. Study on stress and deformation of K-TIG welded joint[J]. Transactions of the China Welding Institution, 2019, 40(11): 125 - 132