In this paper, the experimental materials of Al2O3 ceramic and pure Ti metal were modified by metals Mo and Ti by magnetron sputtering and brazed using Au filling metal. The effect of joining process and Ti metallizing layer thickness on the microstructure and mechanical property of the joints was investigated. The results show that the microstructure of the Al2O3/Ti joint mainly consisted of Au braze and (Au, Mo)ss. There were a few (Ti, Mo)ss and TixAuy intermetallic compounds (IMCs) among the (Au, Mo)ss. A few TiO2 and TixAuy IMCs were also observed at the Al2O3/braze interface and in the weld. The kind of phases in the weld was free from influence of bonding temperature, holding time and Ti metallizing layer thickness. However, both the number and distribution of phases in the weld change with bonding temperature, holding time and Ti metallizing layer thickness. The shear strength of joints was changed by the bonding temperature, holding time and Ti metallizing layer thickness because these factors influenced the distribution uniformity of solid solution and the number of IMCs in the weld. When the thickness of Ti metallized layer was 0.2 μm, maximum shear strength of 138 MPa was achieved at 1 080℃ for 5 min.
LIN Panpan
,
LIN Tiesong
,
HE Peng
,
WANG Maochang
,
YANG Hangao
. Microstructure and mechanical property of Al2O3/Ti joint with biocompatibility[J]. Transactions of The China Welding Institution, 2019
, 40(7)
: 16
-23
.
DOI: 10.12073/j.hjxb.2019400175
[1] Chevalier J, Gremillard L. Ceramics for medical applications:a picture for the next 20 years[J]. Journal of European Ceramic Society, 2009, 29:1245-1255.
[2] Li Y H, Wang F, Li J J. Current developments of biomedical porous Ti-Mo alloys[J]. International Journal of Materials Research, 2017, 108:619-624.
[3] 黄万群,李亚江,王娟,等.陶瓷/金属钎焊与扩散连接的研究现状[J].焊接, 2007(4):11-13 Huang Wanqun, Li Yajiang, Wang Juan, et al. Research status of brazing and diffusion bonding of ceramic metal[J]. Welding&Joining, 2007(4):11-13
[4] Gall M, Botsis J, Janczak-Rusch J. Rellef of the resdiual stresses in ceramic-metal joints by a layered braze strycture[J]. Adcabced Engineering Materials, 2006, 8(3):156-164.
[5] Chuang T H, Yeh M S, Chai Y H. Development of technique for copper metallization on ceramics[J]. Metallurgical and Materials Transactions A, 2000, 1591:101-105.
[6] 熊华平,吴世彪,陈波,等.缓解陶瓷/金属连接接头残余热应力的方法研究进展[J].焊接学报, 2013, 34(9):107-112 Xiong Huaping, Wu Shibiao, Chen Bo, et al. Progress of methods for decreasing residual thermal stresses in ceramic/metal joints[J]. Transactions of the China Welding Institution, 2013, 34(9):107-112
[7] 李卓然,樊建新,冯吉才.氧化铝陶瓷与金属连接的研究现状[J].宇航材料工艺, 2008, 38(4):6-8 Li Zhuoran, Fan Jianxin, Feng Jicai. Process in joining of alumina ceramics to metal[J]. Aerospace Materials and Technology, 2008, 38(4):6-8
[8] 朱永权,张丽霞,任伟,等.表面活化Al2O3陶瓷与5005铝合金真空钎焊[J].焊接学报, 2018, 39(11):78-82 Zhu Yongquan, Zhang Lixia, Ren Wei, et al. Vacuum brazing of active metallized Al2O3 ceramic to 5005 aluminum alloy[J]. Transactions of the China Welding Institution, 2018, 39(11):78-82
[9] Xin C L, Yan J Z, Li N, et al. Microstructural evolution during the brazing of Al2O3 ceramic to kovar alloy by sputtering Ti/Mo films on the ceramic surface[J]. Ceramics International, 2016(42):12586-12593.
[10] 赵文庆,吴爱萍,邹贵生,等.高纯氧化铝与金属钛的钎焊[J].焊接学报, 2006, 27(5):85-88 Zhao Wenqing, Wu Aiping, Zou Guisheng, et al. Brazing between high purity alumina ceramics and titanium[J]. Transactions of the China Welding Institution, 2006, 27(5):85-88
[11] Correia R N, Emiliano J V, Moretto P. Microstructure of diffusional zirconia titaniumand zirconia Ti6Al4V alloy joints[J]. Joining Material Science, 1998(33):215-221.
[12] Agathopoulos S, Correia R N, Joanni E, et al. Interactions at zirconia-Au-tiinterfaces at high temperatures[J]. Key Engineering Materials, 2002, 1:487-490.