Linear friction welding (LFW) test and post-weld heat treatment of welded joints of Ti2AlNb alloy were carried out. The microstructure evolution in recrystallization zone and thermo-mechanical affected zone of Ti2AlNb LFW joint with post heat treatment were analyzed. The results showed that high quality joint of Ti2AlNb without microcrack and microvoid could be formed by LFW. WZ (weld zone) consisted of metastable β phase and few of twisted α2. TMAZ was made of O phase, metastable β phase and much of twisted α2 phase. After heat treatment, metastable β broke down into O lamina precipitate and the size of O lamina increased with the temperature from 700℃ to 900℃. Microhardness increased obviously after heat treatment at 700℃ while it decreased with the increasing of temperature.
HE Jianchao
,
ZHANG Tiancang
,
LI Ju
. Effect of heat treatment on microstructure and hardness of Ti2AlNb linear friction welding joint[J]. Transactions of The China Welding Institution, 2019
, 40(4)
: 119
-124
.
DOI: 10.12073/j.hjxb.2019400111
[1] 郭和平, 曾元松, 李志强. O相合金Ti2AlNb的超塑性研究进展[J]. 航空制造技术, 2009, 10:64-67 Guo Heping, Zeng Yuansong, Li Zhiqiang. Research progress of superplasticity of intermetallic Ti2AlNb orthorhombic alloys[J]. Aeronautical Manufacturing Technology, 2009, 10:64-67
[2] Froes F H, Suryanarayana C, Eliezer D. Review:synthesis, properties and applications of titanium aluminides[J]. Journal of Materials Science, 1992, 27:5113-5140.
[3] Kumpfert J. Intermetallic alloys based on orthorhombic titanium aluminide[J]. Advance Engineering Material, 2001, 3:851-864.
[4] 冯艾寒, 李渤渤, 沈军. Ti2AlNb基合金的研究进展[J]. 材料与冶金学报, 2011, 10(1):30-38 Feng Aihan, Li Bobo, Shen Jun. Recent advances on Ti2AlNb-based alloys[J]. Journal of Materials and Metallurgy, 2011, 10(1):30-38
[5] 吴会强, 冯吉才, 何景山, 等. 电子束焊接TiAl基合金接头组织结构及其裂纹产生的敏感性[J]. 材料工程, 2005, 4:7-10 Wu Huiqiang, Feng Jicai, He Jingshan et al. Structure and crack forming susceptibility of TiAl based alloy joints by electron beam welding[J]. Journal of Materials Engineering, 2005, 4:7-10
[6] 邹贵生, 白海林, 谢二虎. O相合金Ti-22Al-25Nb固态扩散连接[J]. 中国有色金属学报, 2008, 18(4):577-584 Zou Guisheng, Bai Hailin, Xie Erhu, et al. Solid diffusion bonding of Ti-22Al-25Nb O phase alloy[J]. The Chinese Journal of Nonferrous Metals, 2008, 18(4):577-584
[7] 张田仓, 李晶, 季亚娟, 等. TC4钛合金线性摩擦焊接头组织和力学性能[J]. 焊接学报, 2010, 31(2):53-56 Zhang Tiancang, Li Jing, Ji Yajuan, et al. Structure and mechanical properties of TC4 linear friction welding joint[J]. Transactions of the China Welding Institution, 2010, 31(2):53-56
[8] Dalgaard E, Wanjara P, Gholipour J, et al. Linear friction welding of a near-b titanium alloy[J]. Acta Materialia, 2012, 60:770-780.
[9] Vairis A, Frost M. On the extrusion stage of linear friction welding of Ti6Al4V[J]. Materials Science and Engineering, 1999, 271:477-484.
[10] Romero J, Attallah M M, Preuss M, et al. Effect of the forging pressure on the microstructure and residual stress development in Ti-6Al-4V linear friction weld[J]. Acta Materialia, 2009, 57:5582-5592.
[11] Chamanfar A, Jahazib M, Gholipourb J, et al. Maximizing the integrity of linear friction welded Waspaloy[J]. Materials Science and Engineering A, 2012, 555:117-130.
[12] 季亚娟, 刘燕冰, 张田仓, 等. TC4/TC17线性摩擦焊接头组织及力学性能[J]. 焊接学报, 2012, 33(10):109-112 Ji Yajuan, Liu Yanbing, Zhang Tiancang, et al. Structure and mechanical properties of TC4/TC17 linear friction welding joint[J]. Transactions of the China Welding Institution, 2012, 33(10):109-112
[13] Raghavan V. Al-Nb-Ti (aluminum-niobium-titanium)[J]. Journal of Phase Equilibria and Diffusion, 2005, 26(4):360-368.