The coolant liquid lead-bismuth eutectic alloy (LBE) of the accelerator driven subcritical reactor system (ADS) would lead to serious cavitation erosion on the main pump impeller and the first wall cladding material when the liquid LBE flows at a high speed. Welding joint is the weak area in the whole circulation pipeline, and the reasonable heat treatment is the most effective method to improve the performance of the weld area. A suit of ultrasonic cavitation facility was self-designed to the cavitation erosion test. By analyzing the surface topography, roughness and mean pit depth of specimens after being eroded for different time, and combining these erosion results with the microstructure and mechanical properties of weld bead after PWHT, the cavitation behavior of weld bead of CLAM steel after PWHT and the influence of PWHT to the cavitation behavior of weld bead were studied. The results show that the weld bead being quenched and tempered showed the best cavitation erosion resistance. The cavitation erosion resistance of weld bead after being tempered at 760℃ were better than that of weld bead after being tempered at 710℃ or 810℃. The weld bead without PWHT exhibited the poorest cavitation erosion resistance.
LEI Yucheng
,
GUO Xiaokai
,
CHANG Hongxia
,
CHEN Gang
. Effect of PWHT on cavitation erosion resistance of CLAM weld joint in liquid Lead-bismuth eutectic alloy[J]. Transactions of The China Welding Institution, 2018
, 39(7)
: 1
-6
.
DOI: 10.12073/j.hjxb.2018390164
[1] 吴宜灿, 黄群英, 柏云清, 等. 液态铅铋回路设计研制与材料腐蚀实验初步研究[J]. 核科学与工程, 2010,30(3):238-243. Wu Yican, Huang Qunying, Bai Yunqing, et al. Preliminary experimental study on the corrosion of structural steels in liquid lead bismuth loop[J].Chinese Journal of Nuclear Science and Enginee ring, 2010,30(3):238-243.
[2] Chen X, Shen Z, Li P, et al. Compatibility of CLAM steel weldments with static LiPb alloy at 500℃[J]. Fusion Engineering and Design, 2012, 87(9):1565-1569.[DOI:10.1016/j.fusengdes.2012.04.012]
[3] Huang Q. Development status of CLAM steel for fusion application, Journal of Nuclear Materials, 2014(455):649-654.
[4] Zhu Q, Lei Y, Chen X, et al. Microstructure and mechanical properties in TIG welding of CLAM steel[J], Fusion Engineering And Design,2011(86):407-411.
[5] 张小彬. CrNiMo不锈钢表面激光熔覆与合金化抗空蚀涂层研究[D]. 沈阳:东北大学, 2007.
[6] 骆素珍, 敬和民, 郑玉贵, 等. CrMnN双相不锈钢的空泡腐蚀行为研究[J].中国腐蚀与防护学报, 2003, 23(5):276-281. Luo Suzhen, Jing Hemin, Zheng Yugui, et al. Cavitation-corrosion behavior of CrMnN duplex stainless steel[J]. Journal of Chinese Society For Corrosion and Protection, 2003, 23(5):276-281.[DOI:10.3969/j.issn.1005-4537.2003.05.005]
[7] 雷玉成, 顾康家, 朱强, 等. 中国低活马氏体钢熔化焊接头硬度与微观组织[J].焊接学报, 2009,30(11):9-12. Lei Yucheng, Gu Kangjia, Zhu Qiang, et al. Hardness and microstructure of China low activation martensitic steel fusion welded joint[J]. Transactions of the China Welding Institution, 2009,30(11):9-12.[DOI:10.3321/j.issn:0253-360X.2009.11.003]