| Effect of Microstructure on Surface Polishing Performance ofPrehardened 718 Plastic Mold Steel |
| ZHANG Le, XU Zhen, LI Zhi, CHEN Xuan, WU Xiaochun |
| State Key Laboratory of Advanced Special Steel, School of Materials Science and Engineering, Shanghai University, Shanghai 200444, China |
|
|
|
|
Abstract Samples at different positions of prehardened large section 718 plastic mold steel were heat treated, and then mechanically polished and manually polished. The surface roughness was tested. The effect of microstructure on the surface polishing performance was studied. The results show that after heat treatment, the sample with the original microstructure of non-uniform granular bainite had the worst uniformity of microstructure and hardness distribution, leading to the largest surface roughness and the worst polishing performance after polishing. The sample with the original microstructure of uniform granular bainite after heat treatment had the best uniformity of microstructure, and the hardness was relatively large and distributed uniformly; therefore the surface roughness after polishing was the smallest. Moreover, no orange lines or pitting defects appeared on the surface after engineering polishing (professional manual polishing for engineering applications), and the limit of surface roughness reached 0.019 μm; the surface quality met the application requirements of high-end plastic mold steel. The uniform distribution of carbides in the sample with the original microstructure of tempered martensite after heat treatment made the surface polishing performance slightly better than that of the lower bainite sample.
|
|
Received: 29 April 2020
Published: 23 August 2021
|
|
|
|
|
|
| [1] |
HILL H, KUNZE M, HEET C, et al. Correlation of processing route and heat treatment with the abrasive wear resistance of a plastic mold steel[J]. Materialwissenschaft Und Werkstofftechnik, 2012, 43(8):711-718.
|
| [2] |
KLOCKE F, DAMBON O, BEHRENS B. Analysis of defect mechanisms in polishing of tool steels[J]. Production Engineering, 2011, 5(5):475-483.
|
| [3] |
李知伦, 马党参, 迟宏宵, 等. 大型预硬化718塑料模具钢不同区域的抛光性能[J]. 机械工程材料, 2015, 39(2):60-66. LI Z L, MA D S, CHI H X, et al. Polishing performance of different zones in large-size plastic die steel 718[J]. Materials for Mechanical Engineering, 2015, 39(2):60-66.
|
| [4] |
吴代烜. 模具型腔及表面加工处理技术[J]. 中国科技信息, 2014(14):166-167. WU D X, Die cavity and surface processing technology[J]. China Science and Technology Information,2014(14):166-167.
|
| [5] |
王勇围, 郭强, 康爱军, 等. 不同组织类型对3Cr2MnNiMo钢抛光性能的影响[J]. 钢铁研究学报, 2011, 23(5):24-28. WANG Y W, GUO Q, KANG A J, et al. Effect of different microstructures on polishing performance of 3Cr2MnNiMo steel[J]. Journal of Iron and Steel Research, 2011, 23(5):24-28.
|
| [6] |
LUO Y, WU X C, WANG H B, et al. A comparative study on non-quenched and quenched prehardened steel for large section plastic mould[J]. Journal of Materials Processing Technology, 2009, 209(14):5437-5442.
|
| [7] |
WU R M, LI J W, SU Y, et al. Improved uniformity of hardness by continuous low temperature bainitic transformation in prehardened mold steel with large section[J]. Materials Science and Engineering:A,2017,706:15-21.
|
| [8] |
DAMBON O, DEMMER A, PETERS J. Surface interactions in steel polishing for the precision tool making[J]. CIRP Annals, 2006, 55(1):609-612.
|
| [9] |
YU W T, LI J, SHI C B, et al. Effect of spheroidizing annealing on microstructure and mechanical properties of high-carbon martensitic stainless steel 8Cr13MoV[J]. Journal of Materials Engineering and Performance,2017,26(2):478-487.
|
| [10] |
ZHANG Z, WU X C, ZHOU Q, et al. Effect of microstructure on the impact toughness of a bainitic steel bloom for large plastic molds[J]. International Journal of Minerals,Metallurgy,and Materials,2015,22(8):842-850.
|
| [11] |
GARCIA-MATEO C, PEET M, CABALLERO F G, et al. Tempering of hard mixture of bainitic ferrite and austenite[J].Materials Science and Technology,2004,20(7):814-818.
|
| [12] |
刘诗汉, 陈大融. 双相钢空蚀破坏的力学机制[J]. 金属学报, 2009, 45(5):519-526. LIU S H, CHEN D R. Mechanics mechanism of duplex steel cavitation damage[J]. Acta Metallurgica Sinica, 2009, 45(5):519-526.
|
| [13] |
SHARMA L, CHHIBBER R. Effect of heat treatment on mechanical properties and corrosion behaviour of API X70 linepipe steel in different environments[J]. Transactions of the Indian Institute of Metals, 2019, 72(1):93-110.
|
| [1] |
WU Xiaoquan, YAO Dengcan, ZHANG Daoda, YAN Hong, HU Zhi. Microstructure and Properties of Laser Cladding WC Reinforced Ni-Based Alloy Cladding Layer on AlSi7Mg Aluminum Alloy Surface[J]. Materials For Mechanical Engineering, 2021, 45(9): 67-72. |
| [2] |
LIU Yihui, LI Bao, CHEN Sijie, DING Guangzhu, LI Shihui. Effect of Postweld Heat Treatment on Microstructure and Mechanical Properties ofSIMP Steel Joint by Transient Liquid Phase Diffusion Bonding[J]. Materials For Mechanical Engineering, 2021, 45(8): 77-80,86. |
| [3] |
PAN Libo, ZHOU Wenqiang, TAN Wen, WANG Junlin, ZUO Zhijiang. Microstructure and Mechanical Properties of 780 MPa Dual Phase Steels with Different Chemical Composition[J]. Materials For Mechanical Engineering, 2021, 45(8): 45-48,54. |
| [4] |
ZHANG Min, DU Mingke, ZHANG Yunlong, WANG Gang, ZHU Ziyue. Microstructure and Property of Dissimilar Steel Welded Joint ofQ345B Low Carbon Steel and 20Mn23Al Non-magnetic Steel[J]. Materials For Mechanical Engineering, 2021, 45(8): 66-71. |
| [5] |
FENG Juning, TAN Fengliang, LI Hongjuan, ZENG Bing, WANG Li, YE Qinzheng. Effect of Rapid Spheroidizing Annealing on Microstructure and Hardness of SKS51 Die Steel[J]. Materials For Mechanical Engineering, 2021, 45(8): 87-90,97. |
| [6] |
ZHANG Dalei, LI Yuanyuan. Effect of High Pressure Heat Treatment on Microstructure and Mechanical Properties of TC9 Titanium Alloy[J]. Materials For Mechanical Engineering, 2021, 45(8): 72-76. |
| [7] |
XU Huanhuan, LIN Chen, LIU Jia, ZHANG Liang, SHEN Jingyi. Effect of CeO2 Adding Content on Microstructure and Properties of Laser Cladding WC Reinforced Nickel-Based Alloy Coating[J]. Materials For Mechanical Engineering, 2021, 45(7): 27-34. |
| [8] |
HE Weiwei, CHEN Junzhou, HAO Min, DAI Shenglong. Hot Deformation Behavior and Processing Map of WE43 Magnesium Alloy[J]. Materials For Mechanical Engineering, 2021, 45(7): 69-74. |
| [9] |
HAN Yuchen, XING Shilong, JIANG Chuanhai. Effect of Y2O3 Nanoparticle on Microstructure and Electrochemical CorrosionProperties of Electroplated Ni-W Coating[J]. Materials For Mechanical Engineering, 2021, 45(5): 22-26. |
| [10] |
MA Changwen, DI Guobiao, WANG Kaikai, HUANG Leqing, LU Shiping. Effect of On-line Quenching on Microstructure Transition andMechanical Properties of High-Strength Steel Plate[J]. Materials For Mechanical Engineering, 2021, 45(5): 34-38. |
| [11] |
SHANG Changpei, YANG Fan, XIA Zhiping. Microstructure and Mechanical Properties of WE54 Alloy after Deformation under Different Speeds[J]. Materials For Mechanical Engineering, 2021, 45(5): 56-62. |
| [12] |
ZHAO Yong, SU Haijun, ZHANG Jun, LIU Lin, FU Hengzhi. Recent Progress on Directional Solidification of Nickel-BasedSuperalloys with Magnetic Field[J]. Materials For Mechanical Engineering, 2021, 45(5): 1-7,44. |
| [13] |
ZHANG Weichen, LI Jiuxiao, YANG Dongye, ZHANG Xinyue, ZHENG Lixin, ZHANG Yutong, HE Linghuan. Microstructure and Mechanical Properties of in-situ Synthesized TiB+La2O3/TC4Titanium Matrix Composite by Selective Laser Melting[J]. Materials For Mechanical Engineering, 2021, 45(5): 67-70,75. |
| [14] |
HUANG Yiping, LI Shaolin, LIU Hailang, JIANG Jianbo, PENG Zhiguo, TAN Yi. Effect of Applied Magnetic Field on Electron Beam Welding Formability[J]. Materials For Mechanical Engineering, 2021, 45(4): 35-39,45. |
| [15] |
ZHENG Shaoxian, XU Longqiang, DU Baofeng, LI Gang. Microstructure and Corrosion Resistance of 1Cr18Ni9Ti Stainless Steel Joint by Pulsed Ultra-Narrow-Gap Welding[J]. Materials For Mechanical Engineering, 2021, 45(4): 13-18. |
|
|
|
|