| Finite Element Simulation of Mechanical Properties of Selective Laser Melted Ti-6Al-4V Alloy at High Strain Rates |
| LI Ying1,2, WANG Shaohui1, ZHANG Ting1,2, LIU Chuanxin1, WU Haihui1, CHAI Xianghai1 |
1. Shanghai Engineering Research Center of Civil Aero Engine, AECC Commercial Aircraft Engine Co., Ltd., Shanghai 200241, China;
2. Key Laboratory of High Performance Fibers&Products, Ministry of Education, Donghua University, Shanghai 201620, China |
|
|
|
|
Abstract Ti-6Al-4V alloy was prepared by selective laser melting (SLM) technique. After post vacuum annealing and hot isostatic pressing treatment, the mechanical properties of the alloy at quasi-static and high strain rates (500-3 000 s-1) were studied. The calibration of bi-linear material model was implemented; the obtained material parameters were applied to the finite element simulation of Hopkinson compression test, and the simulation results were compared with the test results. The results show that the microstructure of SLM formed alloy after vacuum annealing and hot isostatic pressing treatment was composed of α phase and β phase with the net basket structure morphology. Compared with that under quasi-static condition, the percentage elongation after fracture of the SLM formed alloy at high strain rates was improved significantly. The normalized true stress-true strain curve obtained by simulation was consistent with test results, and the average relative error was 2.5%, indicating the material parameters was recommended for the subsequent transient impact simulation analysis.
|
|
Received: 11 February 2019
Published: 28 March 2020
|
|
|
|
|
|
| [1] |
WANG Xiao, WANG Huaiming, QI Junfeng, LI Zhijie, ZHANG Yang. Numerical Simulation of Properties of Auxetic Elliptical Porous AlSi10Mg Alloy Prepared by Selective Laser Melting[J]. Materials For Mechanical Engineering, 2020, 44(3): 62-67. |
| [2] |
SUN Jing, ZHU Xiaogang, LI Peng, WANG Xuqin, QIU Lianfang, WANG Fei, WANG Lianfeng, WU Wenheng, GU Zheming. Effect of Laser Bulk Energy Density on Densification Behavior of TC4 Titanium Alloy by SLM[J]. Materials For Mechanical Engineering, 2020, 44(1): 51-56. |
| [3] |
LI Yong, XU Hejun, BA Fahai, HE Beibei, LI Kai. Finite Element Simulation and High-temperature Creep Property of Hastelloy-X Superalloy Prepared by Selective Laser Melting[J]. Materials For Mechanical Engineering, 2019, 43(9): 60-67. |
| [4] |
ZHOU Ping, GUO Weiguo, LI Yanping. High Strain-Rate Shear Behavior of TiB2/2024Al Composite at Different Temperatures[J]. Materials For Mechanical Engineering, 2018, 42(9): 61-64. |
| [5] |
LI Jiuxiao, LI Mingpei, YANG Dongye, HE Bo. Research Progress on Residual Stress in Metal Component Manufactured by Selective Laser Melting[J]. Materials For Mechanical Engineering, 2018, 42(8): 1-6. |
| [6] |
LIAO Wenjun, FAN Enxiang, FU Chao. Microstructure and Tensile Properties of Hastelloy-X Alloy Prepared by Selective Laser Melting[J]. Materials For Mechanical Engineering, 2018, 42(7): 16-22,27. |
| [7] |
HUANG Biao, YAN Hongge, CHEN Jihua, XIA Weijun, SU Bin, CHENG Meixin. Effects of Rolling Process Parameters on Microstructure and Tensile Properties of ZK60 Magnesium Alloy[J]. Materials For Mechanical Engineering, 2018, 42(6): 69-73. |
| [8] |
LIU Yan, LI Zongyi, ZHANG Xiaogang, ZHANG Hao. Selective Laser Melting Forming Process of 316L Stainless Steel Powder and Properties of Formed Parts[J]. Materials For Mechanical Engineering, 2018, 42(5): 40-44. |
| [9] |
XU Hejun, LI Yong, QI Hai, BA Fahai. Effect of Hot Isostatic Pressing Process on Stress-Rupture Property of Hastelloy X Alloy by Selective Laser Melting[J]. Materials For Mechanical Engineering, 2018, 42(12): 53-57,63. |
| [10] |
CAI Zhen, ZHANG Xiancheng, TU Shantong. Effects of Ultrasonic Surface Rolling Process on Microstructure and Surface Integrity of Ti-6Al-4V Alloy[J]. Materials For Mechanical Engineering, 2018, 42(1): 7-10,17. |
| [11] |
MA Mingtu, LI Jie, ZHAO Yan, WU Emei. Research Progress of Response Characteristics of Metallic Materials for Automotive under High Strain Rates[J]. Materials For Mechanical Engineering, 2017, 41(9): 1-13,24. |
| [12] |
ZHANG Jinkai, CHENG Mengqi, WEI Xingqiao, WU Laizhi, WANG Liqiang, LÜ Weijie. Microstructure and Mechanical Properties of Silver-Loaded Layer on Surface of TC4 Alloy Prepared by Friction Stir Processing[J]. Materials For Mechanical Engineering, 2017, 41(6): 63-68. |
| [13] |
ZHENG Zhen-xing, ZHU De-zhi. Microstructure Characteristic of Adiabatic Shear Band in 55vol% TiB2 Particles Reinforced Aluminum Matrix Composite at High Strain Rates[J]. Materials For Mechanical Engineering, 2017, 41(4): 84-88. |
| [14] |
ZHU Xiao-gang, SUN Jing, WANG Lian-feng, CHENG Ling-yu, WEN Shan-shan, YANG Yang. Microstructure, Properties and Inclined Plane Forming Quality of Aluminum Alloy by Selective Laser Melting[J]. Materials For Mechanical Engineering, 2017, 41(2): 77-80. |
| [15] |
SUN Jing, ZHU Xiaogang, WANG Lianfeng, CHENG Lingyu, ZHANG Chenglin. Effect of Scanning Strategy and Preheating Temperature on Properties of Large-Scale AlSi10Mg Alloy Prepared by Selective Laser Melting[J]. Materials For Mechanical Engineering, 2017, 41(10): 52-57. |
|
|
|
|